C10R
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength460-760MPa
Yield Strength350MPa
Brinell Hardness131HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (+C)
8
A - Min. elongation at fracture (%) (+C)
9
A - Min. elongation at fracture (%) (+C)
10
A - Min. elongation at fracture (%) (+C)
12
R p0.2 0.2% proof strength (MPa) (+C)
350
R p0.2 0.2% proof strength (MPa) (+C)
300
R p0.2 0.2% proof strength (MPa) (+C)
250
R p0.2 0.2% proof strength (MPa) (+C)
200
R p0.2 0.2% proof strength (MPa) (+C)
180
R p0.2 0.2% proof strength (MPa) (+C)
350
+C
Rm - Tensile strength (MPa) (+C)
460-760
Rm - Tensile strength (MPa) (+C)
430-730
Rm - Tensile strength (MPa) (+C)
400-700
Rm - Tensile strength (MPa) (+C)
350-640
Rm - Tensile strength (MPa) (+C)
320-580
Rm - Tensile strength (MPa) (+SH)
310-550
Hardness
Brinell hardness (HBW): (+A)
131
Brinell hardness (HBW): (+N)
85 - 140
Brinell hardness (HBW): (+SH)
92 - 163
Other
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.1207C10R
Standards
EN 10084 EN 10084: 2008 Case hardening steels. Technical delivery conditions
EN 10277-4 EN 10277-4: 2008 Bright steel products. Technical delivery conditions. Case hardening steels