UNS C63200 Aluminum-Nickel Bronze
Bronze
O20 (hot forged and annealed)
Property Overview
Density8.3g/cm³
Elastic Modulus120GPa
Tensile Strength710MPa
Yield Strength310MPa
Brinell HardnessUnknown
Maximum Service Temperature230°C
Chemical Composition
NI
4.0 to 4.8%
MN
1.2 to 2.0%
SI
0 to 0.1%
CU
78.8 to 82.6%
AL
8.7 to 9.5%
PB
0 to 0.020%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
3.5 to 4.3%
Mechanical
Elastic (Young's, Tensile) Modulus
120 GPa
Elongation at Break
17 %
Poisson's Ratio
0.34
Shear Modulus
44 GPa
Shear Strength
440 MPa
Tensile Strength: Ultimate (UTS)
710 MPa
Tensile Strength: Yield (Proof)
310 MPa
Physical
Density
8.3 g/cm 3
Thermal
Latent Heat of Fusion
230 J/g
Maximum Temperature: Mechanical
230 °C
Melting Completion (Liquidus)
1060 °C
Melting Onset (Solidus)
1040 °C
Specific Heat Capacity
440 J/kg-K
Thermal Conductivity
35 W/m-K
Thermal Diffusivity
9.6 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
24 points
Electrical
Electrical Conductivity: Equal Volume
7.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
7.6 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
98 MJ/m 3
Resilience: Unit (Modulus of Resilience)
400 kJ/m 3
Stiffness to Weight: Axial
7.9 points
Stiffness to Weight: Bending
20 points
Strength to Weight: Axial
24 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
29 % relative
Embodied Carbon
3.4 kg CO 2 /kg material
Embodied Energy
55 MJ/kg
Embodied Energy
55 MJ/kg 24 x 10 3 BTU/lb
Embodied Water
380 L/kg
Embodied Water
380 L/kg 45 gal/lb
Registered Designations & Aliases
C63200UNS C63200 Aluminum-Nickel Bronze
Standards
ASTM B124 ASTM B124: Standard Specification for Copper and Copper Alloy Forging Rod, Bar, and Shapes
ASTM B150 ASTM B150: Standard Specification for Aluminum Bronze Rod, Bar, and Shapes
ASTM B150 ASTM B150: Standard Specification for Aluminum Bronze Rod, Bar, and Shapes ASTM B124: Standard Specification for Copper and Copper Alloy Forging Rod, Bar, and Shapes ASTM B283: Standard Specification for Copper and Copper-Alloy Die Forgings (Hot-Pressed) Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
ASTM B283 ASTM B283: Standard Specification for Copper and Copper-Alloy Die Forgings (Hot-Pressed)