C50E
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength580MPa
Yield Strength465MPa
Brinell Hardness217HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%) (+N)
13
A - Min. elongation Lo = 5,65 √ So (%) (+N)
14
A - Min. elongation Lo = 80 mm (%) (+A)
17
A - Min. elongation at fracture (%) (+C)
5
A - Min. elongation at fracture (%) (+C)
6
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
R p0.2 0.2% proof strength (MPa) (+A)
465
R p0.2 0.2% proof strength (MPa) (+A)
465
+A
R p0.2 0.2% proof strength (MPa) (+C)
590
R p0.2 0.2% proof strength (MPa) (+C)
520
R p0.2 0.2% proof strength (MPa) (+C)
440
R p0.2 0.2% proof strength (MPa) (+C)
390
R p0.2 0.2% proof strength (MPa) (+C)
590
+C
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
355
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
320
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
290
Rm - Tensile strength (MPa) (+A)
580
Rm - Tensile strength (MPa) (+C)
770-1100
Rm - Tensile strength (MPa) (+C)
730-1080
Rm - Tensile strength (MPa) (+C)
690-1050
Rm - Tensile strength (MPa) (+C)
650-1030
Rm - Tensile strength (MPa) (+CR)
1050
Rm - Tensile strength (MPa) (+N)
650
Rm - Tensile strength (MPa) (+N)
610
Rm - Tensile strength (MPa) (+N)
590
Rm - Tensile strength (MPa) (+QT)
1050-1650
Hardness
Brinell hardness (HBW): (+A)
217
Brinell hardness (HBW): (+S)
255
Brinell hardness (HBW): (+SH)
181 - 269
Vickers hardness ( HV): (+A)
180
Vickers hardness ( HV): (+CR)
295
Vickers hardness ( HV): (+QT)
325 - 505
Other
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 100
Nominal thickness (mm):
100 - 250
Nominal thickness (mm):
0.3 - 3
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Registered Designations & Aliases
1.1206C50E
Standards
EN 10083-2 EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels
EN 10132-3 EN 10132-3: 2000 Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. Steels for quenching and tempering
EN 10277-5 EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering