C45R
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength620MPa
Yield Strength565MPa
Brinell Hardness207HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%) (+N)
14
A - Min. elongation Lo = 5,65 √ So (%) (+N)
16
A - Min. elongation at fracture (%) (+C)
5
A - Min. elongation at fracture (%) (+C)
6
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
R p0.2 0.2% proof strength (MPa) (+C)
565
R p0.2 0.2% proof strength (MPa) (+C)
500
R p0.2 0.2% proof strength (MPa) (+C)
410
R p0.2 0.2% proof strength (MPa) (+C)
360
R p0.2 0.2% proof strength (MPa) (+C)
310
R p0.2 0.2% proof strength (MPa) (+C)
565
+C
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
340
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
305
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
275
Rm - Tensile strength (MPa) (+C)
750-1050
Rm - Tensile strength (MPa) (+C)
710-1030
Rm - Tensile strength (MPa) (+C)
650-1000
Rm - Tensile strength (MPa) (+C)
630-900
Rm - Tensile strength (MPa) (+C)
580-850
Rm - Tensile strength (MPa) (+N)
620
Rm - Tensile strength (MPa) (+N)
580
Rm - Tensile strength (MPa) (+N)
560
Hardness
Brinell hardness (HBW): (+A)
207
Brinell hardness (HBW): (+S)
255
Brinell hardness (HBW): (+SH)
172 - 242
Other
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 100
Nominal thickness (mm):
100 - 250
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.1201C45R
Standards
EN 10083-2 EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels
EN 10277-5 EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering