C35R
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength550MPa
Yield Strength510MPa
Brinell Hardness154 - 207HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%) (+N)
18
A - Min. elongation Lo = 5,65 √ So (%) (+N)
19
A - Min. elongation at fracture (%) (+C)
6
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
A - Min. elongation at fracture (%) (+C)
9
KV - Impact energy (J) (+QT)
+20° 35
R p0.2 0.2% proof strength (MPa) (+C)
510
R p0.2 0.2% proof strength (MPa) (+C)
420
R p0.2 0.2% proof strength (MPa) (+C)
320
R p0.2 0.2% proof strength (MPa) (+C)
300
R p0.2 0.2% proof strength (MPa) (+C)
270
R p0.2 0.2% proof strength (MPa) (+C)
510
+C
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
300
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
270
Re - Upper yield strength or R p0.2 - 0.2% proof strength (MPa) (+N)
245
Rm - Tensile strength (MPa) (+C)
650-1000
Rm - Tensile strength (MPa) (+C)
600-950
Rm - Tensile strength (MPa) (+C)
580-880
Rm - Tensile strength (MPa) (+C)
550-840
Rm - Tensile strength (MPa) (+C)
520-800
Rm - Tensile strength (MPa) (+N)
550
Rm - Tensile strength (MPa) (+N)
520
Rm - Tensile strength (MPa) (+N)
500
Hardness
Brinell hardness (HBW): (+SH)
154 - 207
Other
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 100
Nominal thickness (mm):
100 - 250
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.1180C35R
Standards
EN 10083-2 EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels
EN 10277-5 EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering