HCT600C
Other Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength600MPa
Yield Strength350-500MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 80 mm (%)
16
R p0.2 0.2% proof strength (MPa)
350-500
Rm - Tensile strength (MPa)
600
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Registered Designations & Aliases
1.0953HCT600C
Standards
EN 10336 EN 10336: 2006 Continuously hot-dip coated and electrolytically coated strip and sheet of multiphase steels for cold forming. Technical delivery conditions
EN 10346 EN 10346: 2009 Continuously hot-dip coated steel flat products. Technical delivery conditions