UNS C60800 Aluminum Bronze
Bronze
Property Overview
Density8.6g/cm³
Elastic Modulus110GPa
Tensile Strength390MPa
Yield Strength150MPa
Brinell HardnessUnknown
Maximum Service Temperature210°C
Chemical Composition
CU
92.5 to 95%
AL
5.0 to 6.5%
AS
0.020 to 0.35%
PB
0 to 0.1%
RES.
Residuals res. | | 0 to 0.5%
RESIDUALS RES.
0 to 0.5%
FE
0 to 0.1%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
55 %
Poisson's Ratio
0.34
Shear Modulus
46 GPa
Shear Strength
290 MPa
Tensile Strength: Ultimate (UTS)
390 MPa
Tensile Strength: Yield (Proof)
150 MPa
Physical
Density
8.6 g/cm 3
Thermal
Latent Heat of Fusion
220 J/g
Maximum Temperature: Mechanical
210 °C
Melting Completion (Liquidus)
1060 °C
Melting Onset (Solidus)
1050 °C
Specific Heat Capacity
410 J/kg-K
Thermal Conductivity
80 W/m-K
Thermal Diffusivity
23 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
14 points
Electrical
Electrical Conductivity: Equal Volume
17 % IACS
Electrical Conductivity: Equal Weight (Specific)
18 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
170 MJ/m 3
Resilience: Unit (Modulus of Resilience)
94 kJ/m 3
Stiffness to Weight: Axial
7.3 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
13 points
Strength to Weight: Bending
14 points
Environmental
Base Metal Price
29 % relative
Embodied Carbon
2.9 kg CO 2 /kg material
Embodied Energy
48 MJ/kg
Embodied Energy
48 MJ/kg 20 x 10 3 BTU/lb
Embodied Water
360 L/kg
Embodied Water
360 L/kg 43 gal/lb
Registered Designations & Aliases
C60800UNS C60800 Aluminum Bronze
Standards
ASTM B111 ASTM B111: Standard Specification for Copper and Copper-Alloy Seamless Condenser Tubes and Ferrule Stock