11SMn37
Carbon & Non-Alloy Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength510-810MPa
Yield Strength440MPa
Brinell Hardness109 - 169HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (+C)
6
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
A - Min. elongation at fracture (%) (+C)
9
R p0.2 0.2% proof strength (MPa) (+C)
440
R p0.2 0.2% proof strength (MPa) (+C)
410
R p0.2 0.2% proof strength (MPa) (+C)
375
R p0.2 0.2% proof strength (MPa) (+C)
305
R p0.2 0.2% proof strength (MPa) (+C)
245
R p0.2 0.2% proof strength (MPa) (+C)
440
+C
Rm - Tensile strength (MPa) (+C)
510-810
Rm - Tensile strength (MPa) (+C)
490-760
Rm - Tensile strength (MPa) (+C)
460-710
Rm - Tensile strength (MPa) (+C)
400-650
Rm - Tensile strength (MPa) (+C)
360-630
Hardness
Brinell hardness (HB):
109 - 169
Brinell hardness (HBW): (+SH)
107 - 169
Other
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.073611SMn37
Standards
EN 10087 EN 10087: 1999 Free cutting steels. Technical delivery conditions for semi-finished products, hot rolled bars and rods
EN 10277-3 EN 10277-3: 2008 Bright steel products. Technical delivery conditions. Free-cutting steels