10S20
Carbon & Non-Alloy Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength520-780MPa
Yield Strength410MPa
Brinell Hardness107 - 156HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
A - Min. elongation at fracture (%) (+C)
9
A - Min. elongation at fracture (%) (+C)
10
A - Min. elongation at fracture (%) (+C)
11
R p0.2 0.2% proof strength (MPa) (+C)
410
R p0.2 0.2% proof strength (MPa) (+C)
390
R p0.2 0.2% proof strength (MPa) (+C)
360
R p0.2 0.2% proof strength (MPa) (+C)
295
R p0.2 0.2% proof strength (MPa) (+C)
235
R p0.2 0.2% proof strength (MPa) (+C)
410
+C
Rm - Tensile strength (MPa) (+C)
520-780
Rm - Tensile strength (MPa) (+C)
490-740
Rm - Tensile strength (MPa) (+C)
460-720
Rm - Tensile strength (MPa) (+C)
410-660
Rm - Tensile strength (MPa) (+C)
380-630
Hardness
Brinell hardness (HB):
107 - 156
Brinell hardness (HBW): (+SH)
105 - 156
Other
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.072110S20
Standards
EN 10087 EN 10087: 1999 Free cutting steels. Technical delivery conditions for semi-finished products, hot rolled bars and rods
EN 10277-3 EN 10277-3: 2008 Bright steel products. Technical delivery conditions. Free-cutting steels