S355J2C
Carbon & Non-Alloy Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength630-950MPa
Yield Strength520MPa
Brinell Hardness146 - 187HB
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) (+C)
6
A - Min. elongation at fracture (%) (+C)
7
A - Min. elongation at fracture (%) (+C)
8
A - Min. elongation at fracture (%) (+C)
9
R p0.2 0.2% proof strength (MPa) (+C)
520
R p0.2 0.2% proof strength (MPa) (+C)
450
R p0.2 0.2% proof strength (MPa) (+C)
350
R p0.2 0.2% proof strength (MPa) (+C)
335
R p0.2 0.2% proof strength (MPa) (+C)
315
R p0.2 0.2% proof strength (MPa) (+C)
520
+C
Rm - Tensile strength (MPa) (+C)
630-950
Rm - Tensile strength (MPa) (+C)
580-880
Rm - Tensile strength (MPa) (+C)
530-850
Rm - Tensile strength (MPa) (+C)
500-770
Rm - Tensile strength (MPa) (+C)
470-740
Hardness
Brinell hardness (HBW): (+SH)
146 - 187
Other
Nominal thickness (mm):
5 - 10
Nominal thickness (mm):
10 - 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.0579S355J2C
Standards
EN 10162 EN 10162: 2003 Cold rolled steel sections. Dimensional and cross-sectional tolerances. Technical delivery conditions
EN 10277-2 EN 10277-2: 2008 Bright steel products. Technical delivery conditions. Steels for general engineering purposes