UNS C22600 Jewelry Bronze
Bronze
H01 (quarter hard)
Property Overview
Density8.7g/cm³
Elastic Modulus110GPa
Tensile Strength330MPa
Yield Strength270MPa
Brinell HardnessUnknown
Maximum Service Temperature170°C
Chemical Composition
CU
86 to 89%
PB
0 to 0.050%
RES.
Residuals res. | | 0 to 0.2%
RESIDUALS RES.
0 to 0.2%
ZN
10.7 to 14%
FE
0 to 0.050%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
33 %
Poisson's Ratio
0.33
Shear Modulus
42 GPa
Shear Strength
220 MPa
Tensile Strength: Ultimate (UTS)
330 MPa
Tensile Strength: Yield (Proof)
270 MPa
Hardness
Rockwell B Hardness
46
Rockwell Superficial 30T Hardness
51
Physical
Density
8.7 g/cm 3
Thermal
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
170 °C
Melting Completion (Liquidus)
1040 °C
Melting Onset (Solidus)
1000 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
170 W/m-K
Thermal Diffusivity
52 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
11 points
Electrical
Electrical Conductivity: Equal Volume
40 % IACS
Electrical Conductivity: Equal Weight (Specific)
42 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
100 MJ/m 3
Resilience: Unit (Modulus of Resilience)
330 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
11 points
Strength to Weight: Bending
12 points
Environmental
Base Metal Price
28 % relative
Embodied Carbon
2.6 kg CO 2 /kg material
Embodied Energy
42 MJ/kg
Embodied Energy
42 MJ/kg 18 x 10 3 BTU/lb
Embodied Water
310 L/kg
Embodied Water
310 L/kg 37 gal/lb
Registered Designations & Aliases
C22600UNS C22600 Jewelry Bronze
Standards
ASTM B134 ASTM B134: Standard Specification for Brass Wire
ASTM B134 ASTM B134: Standard Specification for Brass Wire ASTM B36: Standard Specification for Brass Plate, Sheet, Strip, And Rolled Bar
ASTM B36 ASTM B36: Standard Specification for Brass Plate, Sheet, Strip, And Rolled Bar