P235S
Carbon & Non-Alloy Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength360-480MPa
Yield Strength235MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation Lo = 5,65 √ So (%) (+N)
26
A - Min. elongation Lo = 5,65 √ So (%) (+N)
25
A - Min. elongation at fracture (%) (+N)
20
A - Min. elongation at fracture (%) (+N)
21
KV - Impact energy (J) (+N)
-20° 28
ReH - Minimum yield strength (MPa) (+N)
235
ReH - Minimum yield strength (MPa) (+N)
225
ReH - Minimum yield strength (MPa) (+N)
215
Rm - Tensile strength (MPa) (+N)
360-480
Other
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 60
Nominal thickness (mm):
2 - 2.5
Nominal thickness (mm):
2.5 - 3
Nominal thickness (mm):
3 - 40
Registered Designations & Aliases
1.0112P235S
Standards
EN 10207 EN 10207: 2005 Steels for simple pressure vessels. Technical delivery requirements for plates, strips and bars