S235JRH
Carbon & Non-Alloy Steels
Property Overview
Density-g/cm³
Elastic ModulusUnknown
Tensile Strength360-510MPa
Yield Strength235MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
A - Min. elongation at fracture (%) longitud.,
26
A - Min. elongation at fracture (%) longitud.,
25
A - Min. elongation at fracture (%) longitud.,
24
A - Min. elongation at fracture (%) longitud.,
22
KV - Impact energy (J)
+20° 27
ReH - Minimum yield strength (MPa)
235
ReH - Minimum yield strength (MPa)
225
ReH - Minimum yield strength (MPa)
215
ReH - Minimum yield strength (MPa)
195
Rm - Tensile strength (MPa)
360-510
Rm - Tensile strength (MPa)
350-500
Hardness
+A Soft annealed +AC Annealed to achieve spheroidization of the carbides +AR As rolled +AT Solution annealed +C Cold drawn / hard +CR Cold rolled +FP Treated to ferrite-pearlite structure and hardness range +I Isothermal annealing +LC Cold drawn / soft +M Thermo mechanical rolling +N Normalized +NT Normalized and tempered
+P Precipitation hardened +PE Peeled +QA Air quenched and tempered +QL Liquid quenched and tempered +QT Quenched and tempered +S Treated to improve shearability +SH As rolled and turned +SR Cold drawn and stress relieved +T Tempered +TH Treated to hardness range +WW Warm worked +U Untreated
Other
Nominal thickness (mm):
to 3
Nominal thickness (mm):
3 - 100
Nominal thickness (mm):
100 - 120
Nominal thickness (mm):
to 16
Nominal thickness (mm):
16 - 40
Nominal thickness (mm):
40 - 63
Nominal thickness (mm):
63 - 80
Nominal thickness (mm):
80 - 100
Nominal thickness (mm):
to 40
Nominal thickness (mm):
63 - 100
Registered Designations & Aliases
1.0039S235JRH
Standards
EN 10210-1 EN 10210-1: 2006 Hot finished structural hollow sections of non-alloy and fine grain steels. Technical delivery requirements
EN 10219-1 EN 10219-1: 2006 Cold formed welded structural hollow sections of non-alloy and fine grain steels. Technical delivery requirements