UNS C23400 Red Brass
Brass
H02 (half hard)
Property Overview
Density8.5g/cm³
Elastic Modulus110GPa
Tensile Strength420MPa
Yield Strength360MPa
Brinell HardnessUnknown
Maximum Service Temperature160°C
Chemical Composition
CU
81 to 84%
PB
0 to 0.050%
RES.
Residuals res. | | 0 to 0.2%
RESIDUALS RES.
0 to 0.2%
ZN
15.7 to 19%
FE
0 to 0.050%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
16 %
Poisson's Ratio
0.32
Shear Modulus
42 GPa
Shear Strength
250 MPa
Tensile Strength: Ultimate (UTS)
420 MPa
Tensile Strength: Yield (Proof)
360 MPa
Hardness
Rockwell B Hardness
66
Rockwell Superficial 30T Hardness
61
Physical
Density
8.5 g/cm 3
Thermal
Latent Heat of Fusion
190 J/g
Maximum Temperature: Mechanical
160 °C
Melting Completion (Liquidus)
970 °C
Melting Onset (Solidus)
930 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
120 W/m-K
Thermal Diffusivity
36 mm 2 /s
Thermal Expansion
19 µm/m-K
Thermal Shock Resistance
14 points
Calculated
Resilience: Ultimate (Unit Rupture Work)
62 MJ/m 3
Resilience: Unit (Modulus of Resilience)
600 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
14 points
Strength to Weight: Bending
14 points
Environmental
Base Metal Price
27 % relative
Embodied Carbon
2.6 kg CO 2 /kg material
Embodied Energy
43 MJ/kg
Embodied Energy
43 MJ/kg 19 x 10 3 BTU/lb
Embodied Water
320 L/kg
Embodied Water
320 L/kg 38 gal/lb
Registered Designations & Aliases
C23400UNS C23400 Red Brass
Standards
ASTM B134 ASTM B134: Standard Specification for Brass Wire