UNS C55284 (BCuP-5) Filler Metal

Copper Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.9g/cm³

Elastic Modulus100GPa

Tensile Strength180MPa

Yield StrengthUnknown

Brinell HardnessUnknown

Maximum Service Temperature200°C

Weight Calculator

Chemical Composition

4.8 to 5.2%

79.2 to 80.7%

14.5 to 15.5%

RES.

Residuals res. | | 0 to 0.15%

RESIDUALS RES.

0 to 0.15%

Mechanical

Elastic (Young's, Tensile) Modulus

100 GPa

Poisson's Ratio

0.34

Shear Modulus

38 GPa

Tensile Strength: Ultimate (UTS)

180 MPa

Physical

Density

8.9 g/cm 3

Thermal

Brazing Temperature

700 to 820 °C

Latent Heat of Fusion

180 J/g

Maximum Temperature: Mechanical

200 °C

Melting Completion (Liquidus)

800 °C

Melting Onset (Solidus)

640 °C

Specific Heat Capacity

380 J/kg-K

Thermal Expansion

17 µm/m-K

Thermal Shock Resistance

7.4 points

Calculated

Stiffness to Weight: Axial

6.5 points

Stiffness to Weight: Bending

18 points

Strength to Weight: Axial

5.6 points

Strength to Weight: Bending

8.0 points

Environmental

Embodied Carbon

16 kg CO 2 /kg material

Embodied Energy

260 MJ/kg

Embodied Energy

260 MJ/kg 110 x 10 3 BTU/lb

Registered Designations & Aliases

BCuP-5C55284UNS C55284 (BCuP-5) Filler Metal