UNS C55280 (BCuP-6) Filler Metal

Copper Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.5g/cm³

Elastic Modulus110GPa

Tensile Strength180MPa

Yield StrengthUnknown

Brinell HardnessUnknown

Maximum Service Temperature200°C

Weight Calculator

Chemical Composition

6.8 to 7.2%

90.5 to 91.4%

1.8 to 2.2%

RES.

Residuals res. | | 0 to 0.15%

RESIDUALS RES.

0 to 0.15%

Mechanical

Elastic (Young's, Tensile) Modulus

110 GPa

Poisson's Ratio

0.34

Shear Modulus

40 GPa

Tensile Strength: Ultimate (UTS)

180 MPa

Physical

Density

8.5 g/cm 3

Thermal

Brazing Temperature

730 to 820 °C

Latent Heat of Fusion

190 J/g

Maximum Temperature: Mechanical

200 °C

Melting Completion (Liquidus)

790 °C

Melting Onset (Solidus)

640 °C

Specific Heat Capacity

410 J/kg-K

Thermal Expansion

16 µm/m-K

Thermal Shock Resistance

7.4 points

Calculated

Stiffness to Weight: Axial

6.9 points

Stiffness to Weight: Bending

19 points

Strength to Weight: Axial

5.9 points

Strength to Weight: Bending

8.3 points

Environmental

Embodied Carbon

4.2 kg CO 2 /kg material

Embodied Energy

67 MJ/kg

Embodied Energy

67 MJ/kg 29 x 10 3 BTU/lb

Registered Designations & Aliases

BCuP-6C55280UNS C55280 (BCuP-6) Filler Metal