UNS C55180 (BCuP-1) Filler Metal
Copper Alloys
Property Overview
Density8.6g/cm³
Elastic Modulus110GPa
Tensile Strength200MPa
Yield Strength100MPa
Brinell HardnessUnknown
Maximum Service Temperature200°C
Chemical Composition
P
4.8 to 5.2%
CU
94.7 to 95.2%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
20 %
Poisson's Ratio
0.34
Shear Modulus
41 GPa
Tensile Strength: Ultimate (UTS)
200 MPa
Tensile Strength: Yield (Proof)
100 MPa
Physical
Density
8.6 g/cm 3
Thermal
Brazing Temperature
790 to 930 °C
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
920 °C
Melting Onset (Solidus)
710 °C
Specific Heat Capacity
400 J/kg-K
Thermal Conductivity
200 W/m-K
Thermal Diffusivity
56 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
7.9 points
Calculated
Resilience: Ultimate (Unit Rupture Work)
34 MJ/m 3
Resilience: Unit (Modulus of Resilience)
48 kJ/m 3
Stiffness to Weight: Axial
7.1 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
6.4 points
Strength to Weight: Bending
8.8 points
Environmental
Base Metal Price
29 % relative
Embodied Carbon
2.5 kg CO 2 /kg material
Embodied Energy
39 MJ/kg
Embodied Energy
39 MJ/kg 17 x 10 3 BTU/lb
Embodied Water
290 L/kg
Embodied Water
290 L/kg 35 gal/lb
Registered Designations & Aliases
BCuP-1C55180UNS C55180 (BCuP-1) Filler Metal