EN CR013A (CuAg0.10) Silver-Bearing Tough Pitch Copper
Copper Alloys
Property Overview
Density9g/cm³
Elastic Modulus120GPa
Tensile Strength230MPa
Yield Strength140MPa
Brinell HardnessUnknown
Maximum Service Temperature200°C
Chemical Composition
CU
99.81 to 99.92%
AG
0.080 to 0.12%
BI
0 to 0.00050%
O
0 to 0.040%
Mechanical
Elastic (Young's, Tensile) Modulus
120 GPa
Elongation at Break
15 %
Poisson's Ratio
0.34
Shear Modulus
43 GPa
Tensile Strength: Ultimate (UTS)
230 MPa
Tensile Strength: Yield (Proof)
140 MPa
Physical
Density
9.0 g/cm 3
Thermal
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
1090 °C
Melting Onset (Solidus)
1040 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
390 W/m-K
Thermal Diffusivity
110 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
8.1 points
Electrical
Electrical Conductivity: Equal Volume
100 % IACS
Electrical Conductivity: Equal Weight (Specific)
100 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
31 MJ/m 3
Resilience: Unit (Modulus of Resilience)
83 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
7.1 points
Strength to Weight: Bending
9.3 points
Environmental
Base Metal Price
35 % relative
Embodied Carbon
2.7 kg CO 2 /kg material
Embodied Energy
42 MJ/kg
Embodied Energy
42 MJ/kg 18 x 10 3 BTU/lb
Embodied Water
390 L/kg
Embodied Water
390 L/kg 46 gal/lb
Registered Designations & Aliases
CuAg0.10EN CR013A (CuAg0.10) Silver-Bearing Tough Pitch Copper
Standards
EN 1976 EN 1976: Copper and copper alloys - Cast unwrought copper products