EN CR006A (Cu-FRTP) Fire-Refined Tough Pitch Copper
Other
Property Overview
Density9g/cm³
Elastic Modulus120GPa
Tensile Strength230MPa
Yield Strength140MPa
Brinell HardnessUnknown
Maximum Service Temperature200°C
Chemical Composition
CU
99.9 to 100%
AG
0 to 0.015%
O
0 to 0.1%
Mechanical
A - Min. elongation Lo = 50mm (%) (R240)
8
A - Min. elongation Lo = 50mm (%) (R290)
4
A - Min. elongation at fracture (%) (R240)
15
A - Min. elongation at fracture (%) (R290)
6
Elastic (Young's, Tensile) Modulus
120 GPa
Elongation at Break
15 %
Poisson's Ratio
0.34
R p0.2 0.2% proof strength (MPa) (R240)
180
R p0.2 0.2% proof strength (MPa) (R290)
250
Shear Modulus
43 GPa
Tensile Strength: Ultimate (UTS)
230 MPa
Tensile Strength: Yield (Proof)
140 MPa
Hardness
Vickers hardness ( HV): (H065)
65 - 95
Vickers hardness ( HV): (H090)
90 - 110
Physical
Density
9.0 g/cm 3
Thermal
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C
Melting Completion (Liquidus)
1090 °C
Melting Onset (Solidus)
1040 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
380 W/m-K
Thermal Diffusivity
110 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
8.1 points
Other
H
Material condition designated by the minimum value of hardness requirement for the product with mandatory hardness requirements
R
Material condition designated by the minimum value of tensile strength requirement for the product with mandatory tensile strength and elongation requirements
Calculated
Resilience: Ultimate (Unit Rupture Work)
31 MJ/m 3
Resilience: Unit (Modulus of Resilience)
83 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
7.1 points
Strength to Weight: Bending
9.3 points
Environmental
Base Metal Price
31 % relative
Embodied Carbon
2.6 kg CO 2 /kg material
Embodied Energy
41 MJ/kg
Embodied Energy
41 MJ/kg 18 x 10 3 BTU/lb
Embodied Water
320 L/kg
Embodied Water
320 L/kg 38 gal/lb
Registered Designations & Aliases
CW006ACu-FRTPCu-FRTPEN CR006A (Cu-FRTP) Fire-Refined Tough Pitch Copper
Standards
EN 12163 EN 12163: 1998 Copper and copper alloys. Rod for general purposes
EN 1652 EN 1652: 1998 Copper and copper alloys. Plate, sheet, strip and circles for general purposes
EN 1976 EN 1976: 1998 Copper and copper alloys. Cast unwrought copper products
EN 1976 EN 1976: Copper and copper alloys - Cast unwrought copper products