UNS C97300 Leaded Nickel Silver
Nickel Alloys
Property Overview
Density8.6g/cm³
Elastic Modulus110GPa
Tensile Strength230MPa
Yield Strength110MPa
Brinell HardnessUnknown
Maximum Service Temperature150°C
Chemical Composition
NI
11 to 14%
SI
0 to 0.15%
P
0 to 0.050%
S
0 to 0.080%
CU
53 to 58%
AL
0 to 0.0050%
PB
8.0 to 11%
RES.
Residuals res. | | 0 to 1.0%
RESIDUALS RES.
0 to 1.0%
SB
0 to 0.35%
SN
1.5 to 3.0%
ZN
17 to 25%
FE
0 to 1.5%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
9.0 %
Poisson's Ratio
0.33
Shear Modulus
40 GPa
Tensile Strength: Ultimate (UTS)
230 MPa
Tensile Strength: Yield (Proof)
110 MPa
Physical
Density
8.6 g/cm 3
Thermal
Latent Heat of Fusion
180 J/g
Maximum Temperature: Mechanical
150 °C
Melting Completion (Liquidus)
1040 °C
Melting Onset (Solidus)
1010 °C
Specific Heat Capacity
370 J/kg-K
Thermal Conductivity
29 W/m-K
Thermal Diffusivity
9.3 mm 2 /s
Thermal Expansion
19 µm/m-K
Thermal Shock Resistance
8.0 points
Electrical
Electrical Conductivity: Equal Volume
6.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
6.3 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
18 MJ/m 3
Resilience: Unit (Modulus of Resilience)
59 kJ/m 3
Stiffness to Weight: Axial
7.0 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
7.6 points
Strength to Weight: Bending
9.8 points
Environmental
Base Metal Price
30 % relative
Embodied Carbon
3.7 kg CO 2 /kg material
Embodied Energy
59 MJ/kg
Embodied Energy
59 MJ/kg 25 x 10 3 BTU/lb
Embodied Water
330 L/kg
Embodied Water
330 L/kg 39 gal/lb
Registered Designations & Aliases
C97300UNS C97300 Leaded Nickel Silver
Standards
ASTM B271 ASTM B271: Standard Specification for Copper-Base Alloy Centrifugal Castings
ASTM B271 ASTM B271: Standard Specification for Copper-Base Alloy Centrifugal Castings ASTM B505: Standard Specification for Copper Alloy Continuous Castings Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993
ASTM B505 ASTM B505: Standard Specification for Copper Alloy Continuous Castings