EN CC380H (CuNi10Fe1Mn1-C) Copper-Nickel
Nickel Alloys
Property Overview
Density8.9g/cm³
Elastic Modulus120GPa
Tensile Strength280MPa
Yield Strength120MPa
Brinell Hardness80HB
Maximum Service Temperature220°C
Chemical Composition
C
CuNi10Fe1Mn1-C ( CC380H ) Copper-nickel alloy Chemical composition. Equivalents of CuNi10Fe1Mn1-C ( CC380H ). Standards.1 Mechanical Properties. Hardness%
NI
9.0 to 11%
MN
1.0 to 1.5%
SI
0 to 0.1%
CU
84.5 to 89%
NB
0 to 1.0%
AL
0 to 0.010%
PB
0 to 0.030%
ZN
0 to 0.5%
FE
1.0 to 1.8%
Mechanical
A - Min. elongation at fracture (%) (GS)
20
A - Min. elongation at fracture (%) (GZ) or (GC)
25
Elastic (Young's, Tensile) Modulus
120 GPa
Elongation at Break
26 %
Poisson's Ratio
0.34
R p0.2 0.2% proof strength (MPa) (GS)
120
R p0.2 0.2% proof strength (MPa) (GZ) or (GC)
100
Rm - Tensile strength (MPa) (GS)
280
Rm - Tensile strength (MPa) (GZ) or (GC)
280
Shear Modulus
47 GPa
Tensile Strength: Ultimate (UTS)
310 MPa
Tensile Strength: Yield (Proof)
120 MPa
Hardness
Brinell Hardness
80
Brinell hardness (HBW): (GS) or (GZ) or (GC)
70
Physical
Density
8.9 g/cm 3
Thermal
Latent Heat of Fusion
220 J/g
Maximum Temperature: Mechanical
220 °C
Melting Completion (Liquidus)
1130 °C
Melting Onset (Solidus)
1080 °C
Specific Heat Capacity
390 J/kg-K
Thermal Conductivity
46 W/m-K
Thermal Diffusivity
13 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
11 points
Electrical
Electrical Conductivity: Equal Volume
11 % IACS
Electrical Conductivity: Equal Weight (Specific)
11 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
65 MJ/m 3
Resilience: Unit (Modulus of Resilience)
59 kJ/m 3
Stiffness to Weight: Axial
7.8 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
9.8 points
Strength to Weight: Bending
12 points
Environmental
Base Metal Price
36 % relative
Embodied Carbon
3.8 kg CO 2 /kg material
Embodied Energy
58 MJ/kg
Embodied Energy
58 MJ/kg 25 x 10 3 BTU/lb
Embodied Water
300 L/kg
Embodied Water
300 L/kg 35 gal/lb
Registered Designations & Aliases
CC380HCuNi10Fe1Mn1-CCuNi10Fe1Mn1-CEN CC380H (CuNi10Fe1Mn1-C) Copper-Nickel
Standards
EN 1982 EN 1982: 2008 Copper and copper alloys. Ingots and castings
EN 1982 EN 1982: Copper and copper alloys - Ingots and castings