UNS C95600 Silicon-Aluminum Bronze
Bronze
Property Overview
Density8.3g/cm³
Elastic Modulus110GPa
Tensile Strength500MPa
Yield Strength230MPa
Brinell HardnessUnknown
Maximum Service Temperature210°C
Chemical Composition
NI
0 to 0.25%
SI
1.8 to 3.2%
CU
88 to 92.2%
AL
6.0 to 8.0%
RES.
Residuals res. | | 0 to 1.0%
RESIDUALS RES.
0 to 1.0%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
15 %
Poisson's Ratio
0.34
Shear Modulus
42 GPa
Tensile Strength: Ultimate (UTS)
500 MPa
Tensile Strength: Yield (Proof)
230 MPa
Physical
Density
8.3 g/cm 3
Thermal
Latent Heat of Fusion
260 J/g
Maximum Temperature: Mechanical
210 °C
Melting Completion (Liquidus)
1000 °C
Melting Onset (Solidus)
980 °C
Specific Heat Capacity
430 J/kg-K
Thermal Conductivity
39 W/m-K
Thermal Diffusivity
11 mm 2 /s
Thermal Expansion
17 µm/m-K
Thermal Shock Resistance
18 points
Electrical
Electrical Conductivity: Equal Volume
8.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.7 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
60 MJ/m 3
Resilience: Unit (Modulus of Resilience)
230 kJ/m 3
Stiffness to Weight: Axial
7.5 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
17 points
Strength to Weight: Bending
17 points
Environmental
Base Metal Price
28 % relative
Embodied Carbon
3.0 kg CO 2 /kg material
Embodied Energy
50 MJ/kg
Embodied Energy
50 MJ/kg 21 x 10 3 BTU/lb
Embodied Water
360 L/kg
Embodied Water
360 L/kg 43 gal/lb
Registered Designations & Aliases
C95600UNS C95600 Silicon-Aluminum Bronze
Standards
ASTM B148 ASTM B148: Standard Specification for Aluminum-Bronze Sand Castings