Hardened M43 Tool Steel
Tool Steels
Property Overview
Density8.2g/cm³
Elastic Modulus200GPa
Tensile Strength2290MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
1.2 to 1.3%
CR
3.5 to 4.3%
NI
0 to 0.3%
MO
7.5 to 8.5%
MN
0.2 to 0.4%
SI
0.15 to 0.65%
P
0 to 0.030%
S
0 to 0.030%
CU
0 to 0.25%
V
1.5 to 1.8%
CO
7.8 to 8.8%
W
2.3 to 3.0%
FE
70.8 to 76%
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Poisson's Ratio
0.29
Shear Modulus
77 GPa
Tensile Strength: Ultimate (UTS)
2290 MPa
Hardness
Rockwell C Hardness
71
Physical
Density
8.2 g/cm 3
Thermal
Latent Heat of Fusion
270 J/g
Melting Completion (Liquidus)
1550 °C
Melting Onset (Solidus)
1500 °C
Specific Heat Capacity
450 J/kg-K
Thermal Conductivity
19 W/m-K
Thermal Diffusivity
5.3 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
71 points
Calculated
PREN (Pitting Resistance)
35
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
77 points
Strength to Weight: Bending
47 points
Environmental
Base Metal Price
33 % relative
Embodied Carbon
8.5 kg CO 2 /kg material
Embodied Energy
120 MJ/kg
Embodied Energy
120 MJ/kg 53 x 10 3 BTU/lb
Embodied Water
140 L/kg
Embodied Water
140 L/kg 17 gal/lb
Registered Designations & Aliases
Hardened M43 Tool Steel
Standards
ASTM A600 ASTM A600: Standard Specification for Tool Steel High Speed
ASTM A600 ASTM A600: Standard Specification for Tool Steel High Speed Tool Steels, 5th ed., George Roberts et al., 1998 Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016