Hardened L6 Tool Steel
Tool Steels
Property Overview
Density7.8g/cm³
Elastic Modulus190GPa
Tensile Strength2090MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0.65 to 0.75%
CR
0.6 to 1.2%
NI
1.3 to 2.0%
MO
0 to 0.5%
MN
0.25 to 0.8%
SI
0 to 0.5%
P
0 to 0.030%
S
0 to 0.030%
CU
0 to 0.25%
V
0 to 0.3%
FE
93.6 to 97.3%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Poisson's Ratio
0.29
Shear Modulus
72 GPa
Tensile Strength: Ultimate (UTS)
2090 MPa
Hardness
Rockwell C Hardness
65
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Melting Completion (Liquidus)
1450 °C
Melting Onset (Solidus)
1410 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
42 W/m-K
Thermal Diffusivity
11 mm 2 /s
Thermal Expansion
11 µm/m-K
Thermal Shock Resistance
70 points
Electrical
Electrical Conductivity: Equal Volume
7.6 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.7 % IACS
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
74 points
Strength to Weight: Bending
46 points
Environmental
Base Metal Price
3.6 % relative
Embodied Carbon
2.0 kg CO 2 /kg material
Embodied Energy
28 MJ/kg
Embodied Energy
28 MJ/kg 12 x 10 3 BTU/lb
Embodied Water
54 L/kg
Embodied Water
54 L/kg 6.5 gal/lb
Registered Designations & Aliases
Hardened L6 Tool Steel
Standards
ASTM A681 ASTM A681: Standard Specification for Tool Steels Alloy
SAE J437 SAE J437: Selection and Heat Treatment of Tool and Die Steels
SAE J437 SAE J437: Selection and Heat Treatment of Tool and Die Steels ASTM A681: Standard Specification for Tool Steels Alloy Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016