Hardened W2 Tool Steel
Tool Steels
Property Overview
Density7.8g/cm³
Elastic Modulus190GPa
Tensile Strength2400MPa
Yield StrengthUnknown
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
C
0.85 to 1.5%
CR
0 to 0.15%
NI
0 to 0.2%
MO
0 to 0.1%
MN
0.35 to 0.74%
SI
0.1 to 0.4%
P
0 to 0.025%
S
0 to 0.025%
CU
0 to 0.2%
V
0.15 to 0.35%
W
0 to 0.15%
FE
96.2 to 98.6%
Mechanical
Elastic (Young's, Tensile) Modulus
190 GPa
Poisson's Ratio
0.29
Shear Modulus
72 GPa
Tensile Strength: Ultimate (UTS)
2400 MPa
Hardness
Rockwell C Hardness
74
Physical
Density
7.8 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Melting Completion (Liquidus)
1450 °C
Melting Onset (Solidus)
1410 °C
Specific Heat Capacity
470 J/kg-K
Thermal Conductivity
45 W/m-K
Thermal Diffusivity
12 mm 2 /s
Thermal Expansion
12 µm/m-K
Thermal Shock Resistance
80 points
Electrical
Electrical Conductivity: Equal Volume
7.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.3 % IACS
Calculated
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
86 points
Strength to Weight: Bending
51 points
Environmental
Base Metal Price
2.3 % relative
Embodied Carbon
2.0 kg CO 2 /kg material
Embodied Energy
29 MJ/kg
Embodied Energy
29 MJ/kg 12 x 10 3 BTU/lb
Embodied Water
48 L/kg
Embodied Water
48 L/kg 5.7 gal/lb
Registered Designations & Aliases
Hardened W2 Tool Steel
Standards
ASTM A686 ASTM A686: Standard Specification for Tool Steel, Carbon
ASTM A686 ASTM A686: Standard Specification for Tool Steel, Carbon Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016