ASTM A439 Type D-2C (F43002) Cast Iron
Cast Iron
Property Overview
Density7.9g/cm³
Elastic Modulus180GPa
Tensile Strength450MPa
Yield Strength220MPa
Brinell Hardness150HB
Maximum Service TemperatureUnknown
Chemical Composition
C
0 to 2.9%
CR
0 to 0.5%
NI
21 to 24%
MN
1.8 to 2.4%
SI
1.0 to 3.0%
P
0 to 0.080%
FE
67.1 to 76.2%
Mechanical
Elastic (Young's, Tensile) Modulus
180 GPa
Elongation at Break
22 %
Poisson's Ratio
0.3
Shear Modulus
70 GPa
Tensile Strength: Ultimate (UTS)
450 MPa
Tensile Strength: Yield (Proof)
220 MPa
Hardness
Brinell Hardness
150
Physical
Density
7.9 g/cm 3
Thermal
Latent Heat of Fusion
290 J/g
Melting Completion (Liquidus)
1390 °C
Melting Onset (Solidus)
1350 °C
Specific Heat Capacity
480 J/kg-K
Thermal Expansion
14 µm/m-K
Thermal Shock Resistance
13 points
Calculated
Resilience: Ultimate (Unit Rupture Work)
83 MJ/m 3
Resilience: Unit (Modulus of Resilience)
140 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
16 points
Strength to Weight: Bending
17 points
Environmental
Base Metal Price
16 % relative
Embodied Carbon
3.6 kg CO 2 /kg material
Embodied Energy
50 MJ/kg
Embodied Energy
50 MJ/kg 21 x 10 3 BTU/lb
Embodied Water
91 L/kg
Embodied Water
91 L/kg 11 gal/lb
Registered Designations & Aliases
ASTM A439 Type D-2C (F43002) Cast IronF43002
Standards
ASTM A439 ASTM A439: Standard Specification for Austenitic Ductile Iron Castings
ASTM A439 ASTM A439: Standard Specification for Austenitic Ductile Iron Castings Cast Iron: Physical and Engineering Properties, Harold T. Angus, 1976