UNS C87400 Silicon Brass
Brass
Property Overview
Density8.3g/cm³
Elastic Modulus110GPa
Tensile Strength390MPa
Yield Strength160MPa
Brinell HardnessUnknown
Maximum Service Temperature170°C
Chemical Composition
SI
2.5 to 4.0%
CU
79 to 85.5%
AL
0 to 0.8%
PB
0 to 1.0%
RES.
Residuals res. | | 0 to 0.8%
RESIDUALS RES.
0 to 0.8%
ZN
12 to 16%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
21 %
Poisson's Ratio
0.33
Shear Modulus
41 GPa
Tensile Strength: Ultimate (UTS)
390 MPa
Tensile Strength: Yield (Proof)
160 MPa
Physical
Density
8.3 g/cm 3
Thermal
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
170 °C
Melting Completion (Liquidus)
920 °C
Melting Onset (Solidus)
820 °C
Specific Heat Capacity
400 J/kg-K
Thermal Conductivity
28 W/m-K
Thermal Diffusivity
8.3 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
14 points
Electrical
Electrical Conductivity: Equal Volume
6.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
7.2 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
65 MJ/m 3
Resilience: Unit (Modulus of Resilience)
120 kJ/m 3
Stiffness to Weight: Axial
7.4 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
13 points
Strength to Weight: Bending
14 points
Environmental
Base Metal Price
27 % relative
Embodied Carbon
2.7 kg CO 2 /kg material
Embodied Energy
44 MJ/kg
Embodied Energy
44 MJ/kg 19 x 10 3 BTU/lb
Embodied Water
310 L/kg
Embodied Water
310 L/kg 37 gal/lb
Registered Designations & Aliases
C87400UNS C87400 Silicon Brass
Standards
ASTM B271 ASTM B271: Standard Specification for Copper-Base Alloy Centrifugal Castings