UNS C83400 Red Brass
Brass
Property Overview
Density8.7g/cm³
Elastic Modulus110GPa
Tensile Strength240MPa
Yield Strength69MPa
Brinell HardnessUnknown
Maximum Service Temperature180°C
Chemical Composition
NI
0 to 1.0%
SI
0 to 0.0050%
P
0 to 0.030%
S
0 to 0.080%
CU
88 to 92%
AL
0 to 0.0050%
PB
0 to 0.5%
RES.
Residuals res. | | 0 to 0.7%
RESIDUALS RES.
0 to 0.7%
SB
0 to 0.25%
SN
0 to 0.2%
ZN
8.0 to 12%
FE
0 to 0.25%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
30 %
Poisson's Ratio
0.33
Shear Modulus
42 GPa
Tensile Strength: Ultimate (UTS)
240 MPa
Tensile Strength: Yield (Proof)
69 MPa
Hardness
Rockwell F Hardness
50
Physical
Density
8.7 g/cm 3
Thermal
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
180 °C
Melting Completion (Liquidus)
1040 °C
Melting Onset (Solidus)
1020 °C
Specific Heat Capacity
380 J/kg-K
Thermal Conductivity
190 W/m-K
Thermal Diffusivity
57 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
8.4 points
Electrical
Electrical Conductivity: Equal Volume
44 % IACS
Electrical Conductivity: Equal Weight (Specific)
46 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
55 MJ/m 3
Resilience: Unit (Modulus of Resilience)
21 kJ/m 3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
7.7 points
Strength to Weight: Bending
9.9 points
Environmental
Base Metal Price
29 % relative
Embodied Carbon
2.7 kg CO 2 /kg material
Embodied Energy
43 MJ/kg
Embodied Energy
43 MJ/kg 18 x 10 3 BTU/lb
Embodied Water
320 L/kg
Embodied Water
320 L/kg 38 gal/lb
Registered Designations & Aliases
C83400UNS C83400 Red Brass