UNS C83300 Leaded Red Brass
Brass
Property Overview
Density8.8g/cm³
Elastic Modulus110GPa
Tensile Strength220MPa
Yield Strength69MPa
Brinell Hardness35HB
Maximum Service Temperature180°C
Chemical Composition
CU
92 to 94%
PB
1.0 to 2.0%
RES.
Residuals res. | | 0 to 0.7%
RESIDUALS RES.
0 to 0.7%
SN
1.0 to 2.0%
ZN
2.0 to 6.0%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
35 %
Poisson's Ratio
0.34
Shear Modulus
42 GPa
Tensile Strength: Ultimate (UTS)
220 MPa
Tensile Strength: Yield (Proof)
69 MPa
Hardness
Brinell Hardness
35
Physical
Density
8.8 g/cm 3
Thermal
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
180 °C
Melting Completion (Liquidus)
1060 °C
Melting Onset (Solidus)
1030 °C
Specific Heat Capacity
380 J/kg-K
Thermal Conductivity
160 W/m-K
Thermal Diffusivity
48 mm 2 /s
Thermal Expansion
18 µm/m-K
Thermal Shock Resistance
7.9 points
Electrical
Electrical Conductivity: Equal Volume
32 % IACS
Electrical Conductivity: Equal Weight (Specific)
33 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
60 MJ/m 3
Resilience: Unit (Modulus of Resilience)
21 kJ/m 3
Stiffness to Weight: Axial
7.0 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
6.9 points
Strength to Weight: Bending
9.2 points
Environmental
Base Metal Price
30 % relative
Embodied Carbon
2.7 kg CO 2 /kg material
Embodied Energy
44 MJ/kg
Embodied Energy
44 MJ/kg 19 x 10 3 BTU/lb
Embodied Water
320 L/kg
Embodied Water
320 L/kg 38 gal/lb
Registered Designations & Aliases
C83300UNS C83300 Leaded Red Brass