Sintered 2014 (ACxx-2014) Aluminum

Wrought Aluminum Alloys

Material conditionT1

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density2.9g/cm³

Elastic Modulus70GPa

Tensile Strength140MPa

Yield Strength97MPa

Brinell HardnessUnknown

Maximum Service Temperature170°C

Weight Calculator

Chemical Composition

0 to 1.2%

3.5 to 5.0%

91.5 to 96.3%

0.2 to 0.8%

RES.

Residuals res. | | 0 to 1.5%

RESIDUALS RES.

0 to 1.5%

Mechanical

Elastic (Young's, Tensile) Modulus

70 GPa

Elongation at Break

2.0 %

Fatigue Strength

65 MPa

Poisson's Ratio

0.33

Shear Modulus

26 GPa

Tensile Strength: Ultimate (UTS)

140 MPa

Tensile Strength: Yield (Proof)

97 MPa

Physical

Density

2.9 g/cm 3

Thermal

Latent Heat of Fusion

390 J/g

Maximum Temperature: Mechanical

170 °C

Melting Completion (Liquidus)

650 °C

Melting Onset (Solidus)

560 °C

Specific Heat Capacity

880 J/kg-K

Thermal Conductivity

130 W/m-K

Thermal Diffusivity

51 mm 2 /s

Thermal Expansion

23 µm/m-K

Thermal Shock Resistance

6.2 points

Electrical

Electrical Conductivity: Equal Volume

33 % IACS

Electrical Conductivity: Equal Weight (Specific)

100 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

2.5 MJ/m 3

Resilience: Unit (Modulus of Resilience)

68 kJ/m 3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

47 points

Strength to Weight: Axial

13 points

Strength to Weight: Bending

20 points

Environmental

Base Metal Price

10 % relative

Embodied Carbon

8.0 kg CO 2 /kg material

Embodied Energy

150 MJ/kg

Embodied Energy

150 MJ/kg 64 x 10 3 BTU/lb

Embodied Water

1150 L/kg

Embodied Water

1150 L/kg 140 gal/lb

Registered Designations & Aliases

ACxx-2014Sintered 2014 (ACxx-2014) Aluminum

Standards

ASTM B595 ASTM B595: Standard Specification for Sintered Aluminum Structural Parts

ASTM B595 ASTM B595: Standard Specification for Sintered Aluminum Structural Parts Sintering of Advanced Materials: Fundamentals and Processes, Zhigang Zak Fang (editor), 2010 Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993