8176 (8176-H24, AlFeSi) Aluminum

Wrought Aluminum Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density2.7g/cm³

Elastic Modulus69GPa

Tensile Strength160MPa

Yield Strength95MPa

Brinell HardnessUnknown

Maximum Service Temperature170°C

Weight Calculator

Chemical Composition

0.030 to 0.15%

98.6 to 99.6%

0 to 0.030%

RES.

Residuals res. | | 0 to 0.15%

RESIDUALS RES.

0 to 0.15%

0 to 0.1%

0.4 to 1.0%

Mechanical

Elastic (Young's, Tensile) Modulus

69 GPa

Elongation at Break

15 %

Fatigue Strength

59 MPa

Poisson's Ratio

0.33

Shear Modulus

26 GPa

Shear Strength

70 MPa

Tensile Strength: Ultimate (UTS)

160 MPa

Tensile Strength: Yield (Proof)

95 MPa

Physical

Density

2.7 g/cm 3

Thermal

Latent Heat of Fusion

400 J/g

Maximum Temperature: Mechanical

170 °C

Melting Completion (Liquidus)

660 °C

Melting Onset (Solidus)

650 °C

Specific Heat Capacity

900 J/kg-K

Thermal Conductivity

230 W/m-K

Thermal Diffusivity

93 mm 2 /s

Thermal Expansion

24 µm/m-K

Thermal Shock Resistance

7.0 points

Electrical

Electrical Conductivity: Equal Volume

61 % IACS

Electrical Conductivity: Equal Weight (Specific)

200 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

21 MJ/m 3

Resilience: Unit (Modulus of Resilience)

66 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

16 points

Strength to Weight: Bending

24 points

Environmental

Base Metal Price

9.5 % relative

Embodied Carbon

8.2 kg CO 2 /kg material

Embodied Energy

150 MJ/kg

Embodied Energy

150 MJ/kg 66 x 10 3 BTU/lb

Embodied Water

1190 L/kg

Embodied Water

1190 L/kg 140 gal/lb

Registered Designations & Aliases

8176 (8176-H24, AlFeSi) Aluminum8176-H24A98176AlFeSiEN AW-8176

Standards

ASTM B800 ASTM B800: Standard Specification for 8000 Series Aluminum Alloy Wire for Electrical Purposes - Annealed and Intermediate Tempers

ASTM B800 ASTM B800: Standard Specification for 8000 Series Aluminum Alloy Wire for Electrical Purposes - Annealed and Intermediate Tempers Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002 Aluminum Standards and Data, Aluminum Association Inc., 2013 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993

EN 573-3 EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products