513.0 (513.0-F, formerly A514.0, GZ42A, A05130) Cast Aluminum
Cast Aluminum Alloys
Property Overview
Density2.7g/cm³
Elastic Modulus68GPa
Tensile Strength200MPa
Yield Strength120MPa
Brinell Hardness55HB
Maximum Service Temperature170°C
Chemical Composition
MN
0 to 0.3%
SI
0 to 0.3%
CU
0 to 0.1%
TI
0 to 0.2%
AL
91.9 to 95.1%
MG
3.5 to 4.5%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
ZN
1.4 to 2.2%
FE
0 to 0.4%
Mechanical
Elastic (Young's, Tensile) Modulus
68 GPa
Elongation at Break
5.7 %
Fatigue Strength
97 MPa
Poisson's Ratio
0.33
Shear Modulus
26 GPa
Shear Strength
170 MPa
Tensile Strength: Ultimate (UTS)
200 MPa
Tensile Strength: Yield (Proof)
120 MPa
Hardness
Brinell Hardness
55
Physical
Density
2.7 g/cm 3
Thermal
Latent Heat of Fusion
390 J/g
Maximum Temperature: Mechanical
170 °C
Melting Completion (Liquidus)
640 °C
Melting Onset (Solidus)
590 °C
Specific Heat Capacity
900 J/kg-K
Thermal Conductivity
130 W/m-K
Thermal Diffusivity
54 mm 2 /s
Thermal Expansion
24 µm/m-K
Thermal Shock Resistance
8.8 points
Electrical
Electrical Conductivity: Equal Volume
34 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
9.8 MJ/m 3
Resilience: Unit (Modulus of Resilience)
100 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
28 points
Environmental
Base Metal Price
9.5 % relative
Embodied Carbon
8.8 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 66 x 10 3 BTU/lb
Embodied Water
1170 L/kg
Embodied Water
1170 L/kg 140 gal/lb
Registered Designations & Aliases
513.0 (513.0-F, formerly A514.0, GZ42A, A05130) Cast Aluminum513.0-FA05130GZ42Aformerly A514.0
Standards
ASTM B108 ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings
ASTM B108 ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993