444.0 (444.0-T4) Cast Aluminum
Cast Aluminum Alloys
Property Overview
Density2.6g/cm³
Elastic Modulus71GPa
Tensile Strength190MPa
Yield Strength83MPa
Brinell Hardness50HB
Maximum Service Temperature170°C
Chemical Composition
MN
0 to 0.35%
SI
6.5 to 7.5%
CU
0 to 0.25%
TI
0 to 0.25%
AL
90.5 to 93.5%
MG
0 to 0.1%
RES.
Residuals res. | | 0 to 0.15%
RESIDUALS RES.
0 to 0.15%
ZN
0 to 0.35%
FE
0 to 0.6%
Mechanical
Elastic (Young's, Tensile) Modulus
71 GPa
Elongation at Break
25 %
Fatigue Strength
51 MPa
Poisson's Ratio
0.33
Shear Modulus
27 GPa
Tensile Strength: Ultimate (UTS)
190 MPa
Tensile Strength: Yield (Proof)
83 MPa
Hardness
Brinell Hardness
50
Physical
Density
2.6 g/cm 3
Thermal
Latent Heat of Fusion
500 J/g
Maximum Temperature: Mechanical
170 °C
Melting Completion (Liquidus)
610 °C
Melting Onset (Solidus)
600 °C
Specific Heat Capacity
900 J/kg-K
Thermal Conductivity
160 W/m-K
Thermal Diffusivity
67 mm 2 /s
Thermal Expansion
22 µm/m-K
Thermal Shock Resistance
8.8 points
Electrical
Electrical Conductivity: Equal Volume
40 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
39 MJ/m 3
Resilience: Unit (Modulus of Resilience)
49 kJ/m 3
Stiffness to Weight: Axial
15 points
Stiffness to Weight: Bending
53 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
28 points
Environmental
Base Metal Price
9.5 % relative
Embodied Carbon
7.9 kg CO 2 /kg material
Embodied Energy
150 MJ/kg
Embodied Energy
150 MJ/kg 64 x 10 3 BTU/lb
Embodied Water
1110 L/kg
Embodied Water
1110 L/kg 130 gal/lb
Registered Designations & Aliases
444.0 (444.0-T4) Cast Aluminum444.0-T4A04440