413.0 (413.0-F, S12B, A04130) Cast Aluminum
Cast Aluminum Alloys
Property Overview
Density2.6g/cm³
Elastic Modulus73GPa
Tensile Strength270MPa
Yield Strength140MPa
Brinell Hardness80HB
Maximum Service Temperature170°C
Chemical Composition
NI
0 to 0.5%
MN
0 to 0.35%
SI
11 to 13%
CU
0 to 1.0%
AL
82.2 to 89%
MG
0 to 0.1%
RES.
Residuals res. | | 0 to 0.25%
RESIDUALS RES.
0 to 0.25%
SN
0 to 0.15%
ZN
0 to 0.5%
FE
0 to 2.0%
Mechanical
Elastic (Young's, Tensile) Modulus
73 GPa
Elongation at Break
2.5 %
Fatigue Strength
130 MPa
Poisson's Ratio
0.33
Shear Modulus
28 GPa
Shear Strength
170 MPa
Tensile Strength: Ultimate (UTS)
270 MPa
Tensile Strength: Yield (Proof)
140 MPa
Hardness
Brinell Hardness
80
Physical
Density
2.6 g/cm 3
Thermal
Latent Heat of Fusion
570 J/g
Maximum Temperature: Mechanical
170 °C
Melting Completion (Liquidus)
590 °C
Melting Onset (Solidus)
580 °C
Specific Heat Capacity
900 J/kg-K
Thermal Conductivity
140 W/m-K
Thermal Diffusivity
59 mm 2 /s
Thermal Expansion
20 µm/m-K
Thermal Shock Resistance
13 points
Electrical
Electrical Conductivity: Equal Volume
35 % IACS
Electrical Conductivity: Equal Weight (Specific)
120 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
5.7 MJ/m 3
Resilience: Unit (Modulus of Resilience)
130 kJ/m 3
Stiffness to Weight: Axial
16 points
Stiffness to Weight: Bending
53 points
Strength to Weight: Axial
29 points
Strength to Weight: Bending
36 points
Environmental
Base Metal Price
9.5 % relative
Embodied Carbon
7.6 kg CO 2 /kg material
Embodied Energy
140 MJ/kg
Embodied Energy
140 MJ/kg 61 x 10 3 BTU/lb
Embodied Water
1040 L/kg
Embodied Water
1040 L/kg 120 gal/lb
Registered Designations & Aliases
413.0 (413.0-F, S12B, A04130) Cast Aluminum413.0-FA04130S12B
Standards
ASTM B85 ASTM B85: Standard Specification for Aluminum-Alloy Die Castings
ASTM B85 ASTM B85: Standard Specification for Aluminum-Alloy Die Castings Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993