332.0 (332.0-T5, formerly F332.0, LM26, SC103A, A03320) Cast Aluminum

Cast Aluminum Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density2.8g/cm³

Elastic Modulus73GPa

Tensile Strength250MPa

Yield Strength190MPa

Brinell Hardness110HB

Maximum Service Temperature170°C

Weight Calculator

Chemical Composition

0 to 0.5%

8.5 to 10.5%

2.0 to 4.0%

0 to 0.25%

80.1 to 89%

0.5 to 1.5%

RES.

Residuals res. | | 0 to 0.5%

RESIDUALS RES.

0 to 0.5%

0 to 1.0%

0 to 1.2%

Mechanical

Elastic (Young's, Tensile) Modulus

73 GPa

Elongation at Break

1.0 %

Fatigue Strength

90 MPa

Poisson's Ratio

0.33

Shear Modulus

27 GPa

Shear Strength

190 MPa

Tensile Strength: Ultimate (UTS)

250 MPa

Tensile Strength: Yield (Proof)

190 MPa

Hardness

Brinell Hardness

110

Physical

Density

2.8 g/cm 3

Thermal

Latent Heat of Fusion

530 J/g

Maximum Temperature: Mechanical

170 °C

Melting Completion (Liquidus)

580 °C

Melting Onset (Solidus)

530 °C

Specific Heat Capacity

880 J/kg-K

Thermal Conductivity

100 W/m-K

Thermal Diffusivity

42 mm 2 /s

Thermal Expansion

21 µm/m-K

Thermal Shock Resistance

12 points

Electrical

Electrical Conductivity: Equal Volume

26 % IACS

Electrical Conductivity: Equal Weight (Specific)

84 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

2.3 MJ/m 3

Resilience: Unit (Modulus of Resilience)

250 kJ/m 3

Stiffness to Weight: Axial

15 points

Stiffness to Weight: Bending

50 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

31 points

Environmental

Base Metal Price

10 % relative

Embodied Carbon

7.8 kg CO 2 /kg material

Embodied Energy

140 MJ/kg

Embodied Energy

140 MJ/kg 61 x 10 3 BTU/lb

Embodied Water

1040 L/kg

Embodied Water

1040 L/kg 120 gal/lb

Registered Designations & Aliases

332.0 (332.0-T5, formerly F332.0, LM26, SC103A, A03320) Cast Aluminum332.0-T5A03320LM26SC103Aformerly F332.0

Standards

ASTM B108 ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings

ASTM B108 ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002