319.0 (SC64D, A03190) Cast Aluminum

Cast Aluminum Alloys

Material conditionT5

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density2.9g/cm³

Elastic Modulus72GPa

Tensile Strength200MPa

Yield Strength180MPa

Brinell Hardness80HB

Maximum Service Temperature170°C

Weight Calculator

Chemical Composition

0 to 0.35%

0 to 0.5%

5.5 to 6.5%

3.0 to 4.0%

0 to 0.25%

85.8 to 91.5%

0 to 0.1%

RES.

Residuals res. | | 0 to 0.5%

RESIDUALS RES.

0 to 0.5%

0 to 1.0%

Mechanical

Elastic (Young's, Tensile) Modulus

72 GPa

Elongation at Break

1.8 %

Fatigue Strength

76 MPa

Poisson's Ratio

0.33

Shear Modulus

27 GPa

Shear Strength

170 MPa

Tensile Strength: Ultimate (UTS)

200 MPa

Tensile Strength: Yield (Proof)

180 MPa

Hardness

Brinell Hardness

Physical

Density

2.9 g/cm 3

Thermal

Latent Heat of Fusion

480 J/g

Maximum Temperature: Mechanical

170 °C

Melting Completion (Liquidus)

600 °C

Melting Onset (Solidus)

540 °C

Solidification (Pattern Maker's) Shrinkage

1.3 %

Specific Heat Capacity

880 J/kg-K

Thermal Conductivity

110 W/m-K

Thermal Diffusivity

44 mm 2 /s

Thermal Expansion

22 µm/m-K

Thermal Shock Resistance

9.2 points

Electrical

Electrical Conductivity: Equal Volume

27 % IACS

Electrical Conductivity: Equal Weight (Specific)

84 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

3.4 MJ/m 3

Resilience: Unit (Modulus of Resilience)

220 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

48 points

Strength to Weight: Axial

19 points

Strength to Weight: Bending

27 points

Environmental

Base Metal Price

10 % relative

Embodied Carbon

7.7 kg CO 2 /kg material

Embodied Energy

140 MJ/kg

Embodied Energy

140 MJ/kg 62 x 10 3 BTU/lb

Embodied Water

1080 L/kg

Embodied Water

1080 L/kg 130 gal/lb

Registered Designations & Aliases

319.0 (SC64D, A03190) Cast AluminumA03190SC64D

Standards

ASTM B108 ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings

ASTM B26 ASTM B26: Standard Specification for Aluminum-Alloy Sand Castings

ASTM B618 ASTM B618: Standard Specification for Aluminum-Alloy Investment Castings

ASTM B618 ASTM B618: Standard Specification for Aluminum-Alloy Investment Castings ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings ASTM B26: Standard Specification for Aluminum-Alloy Sand Castings Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002 Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003 Advanced Materials in Automotive Engineering, Jason Rowe (editor), 2012 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993