Grade Ti-Pd17 Cast Titanium
Titanium Alloys
Property Overview
Density4.5g/cm³
Elastic Modulus110GPa
Tensile Strength270MPa
Yield Strength190MPa
Brinell Hardness200HB
Maximum Service Temperature320°C
Chemical Composition
C
0 to 0.1%
NI
0 to 0.030%
TI
98.9 to 99.96%
H
0 to 0.015%
O
0 to 0.25%
PD
0.040 to 0.080%
RES.
Residuals res. | | 0 to 0.4%
RESIDUALS RES.
0 to 0.4%
FE
0 to 0.2%
Mechanical
Elastic (Young's, Tensile) Modulus
110 GPa
Elongation at Break
22 %
Fatigue Strength
140 MPa
Poisson's Ratio
0.32
Shear Modulus
40 GPa
Tensile Strength: Ultimate (UTS)
270 MPa
Tensile Strength: Yield (Proof)
190 MPa
Hardness
Brinell Hardness
200
Rockwell C Hardness
21
Physical
Density
4.5 g/cm 3
Thermal
Latent Heat of Fusion
420 J/g
Maximum Temperature: Mechanical
320 °C
Melting Completion (Liquidus)
1660 °C
Melting Onset (Solidus)
1610 °C
Specific Heat Capacity
540 J/kg-K
Thermal Conductivity
21 W/m-K
Thermal Diffusivity
8.8 mm 2 /s
Thermal Expansion
8.7 µm/m-K
Thermal Shock Resistance
21 points
Electrical
Electrical Conductivity: Equal Volume
3.6 % IACS
Electrical Conductivity: Equal Weight (Specific)
7.1 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
55 MJ/m 3
Resilience: Unit (Modulus of Resilience)
180 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
35 points
Strength to Weight: Axial
17 points
Strength to Weight: Bending
21 points
Environmental
Embodied Carbon
36 kg CO 2 /kg material
Embodied Energy
600 MJ/kg
Embodied Energy
600 MJ/kg 260 x 10 3 BTU/lb
Embodied Water
230 L/kg
Embodied Water
230 L/kg 27 gal/lb
Registered Designations & Aliases
Grade Ti-Pd17 Cast Titanium
Standards
ASTM B367 ASTM B367: Standard Specification for Titanium and Titanium Alloy Castings
ASTM B367 ASTM B367: Standard Specification for Titanium and Titanium Alloy Castings Titanium and Titanium Alloys: Fundamentals and Applications, Christoph Leyens and Manfred Peters (editors), 2003 Titanium, 2nd ed., G. Lutjering and J. C. Williams, 2007