UNS N10665 (2.4617, NiMo28) Nickel-Molybdenum Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density9.3g/cm³

Elastic Modulus220GPa

Tensile Strength690MPa

Yield Strength400MPa

Brinell HardnessUnknown

Maximum Service Temperature900°C

Weight Calculator

Chemical Composition

0 to 0.020%

0 to 1.0%

64.8 to 74%

26 to 30%

0 to 1.0%

0 to 0.1%

0 to 0.040%

0 to 0.030%

0 to 1.0%

0 to 2.0%

Mechanical

A - Min. elongation at fracture (%) (5d)

Elastic (Young's, Tensile) Modulus

220 GPa

Elongation at Break

45 %

Fatigue Strength

340 MPa

Poisson's Ratio

0.31

R p0.2 0.2% proof strength (MPa)

400

Rm - Tensile strength (MPa)

690

Shear Modulus

84 GPa

Shear Strength

600 MPa

Tensile Strength: Ultimate (UTS)

860 MPa

Tensile Strength: Yield (Proof)

400 MPa

Hardness

Rockwell B Hardness

Physical

Density

9.3 g/cm 3

Thermal

Latent Heat of Fusion

310 J/g

Maximum Temperature: Mechanical

900 °C

Melting Completion (Liquidus)

1620 °C

Melting Onset (Solidus)

1570 °C

Specific Heat Capacity

390 J/kg-K

Thermal Conductivity

11 W/m-K

Thermal Diffusivity

3.1 mm 2 /s

Thermal Expansion

10 µm/m-K

Thermal Shock Resistance

27 points

Electrical

Electrical Conductivity: Equal Volume

1.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

1.2 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

320 MJ/m 3

Resilience: Unit (Modulus of Resilience)

360 kJ/m 3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

22 points

Strength to Weight: Axial

26 points

Strength to Weight: Bending

22 points

Environmental

Base Metal Price

75 % relative

Embodied Carbon

15 kg CO 2 /kg material

Embodied Energy

200 MJ/kg

Embodied Energy

200 MJ/kg 84 x 10 3 BTU/lb

Embodied Water

270 L/kg

Embodied Water

270 L/kg 32 gal/lb

Registered Designations & Aliases

2.4617N10665Ni1066NiMo28NiMo28UNS N10665 (2.4617, NiMo28) Nickel-Molybdenum Alloy

Standards

ASTM B333 ASTM B333: Standard Specification for Nickel-Molybdenum Alloy Plate, Sheet, and Strip

ASTM B333 ASTM B333: Standard Specification for Nickel-Molybdenum Alloy Plate, Sheet, and Strip ASTM B335: Standard Specification for Nickel-Molybdenum Alloy Rod ASTM B462: Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube ASTM B564: Standard Specification for Nickel Alloy Forgings Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009

ASTM B335 ASTM B335: Standard Specification for Nickel-Molybdenum Alloy Rod

ASTM B462 ASTM B462: Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube

ISO 14172 ISO 14172: 2008 Welding consumables. Covered electrodes for manual metal arc welding of nickel and nickel alloys. Classification