UNS N10624 Nickel-Molybdenum Alloy

Nickel Alloys

OverviewChemical CompositionMechanical PropertiesPhysical PropertiesOther Properties

Property Overview

Density9g/cm³
Elastic Modulus220GPa
Tensile Strength810MPa
Yield Strength360MPa
Brinell HardnessUnknown
Maximum Service Temperature930°C
Weight Calculator

Chemical Composition

C
0 to 0.010%
CR
6.0 to 10%
NI
53.9 to 68%
MO
21 to 25%
MN
0 to 1.0%
SI
0 to 0.1%
P
0 to 0.025%
S
0 to 0.010%
CU
0 to 0.5%
AL
0 to 0.5%
CO
0 to 1.0%
FE
5.0 to 8.0%

Mechanical

Elastic (Young's, Tensile) Modulus
220 GPa
Elongation at Break
45 %
Fatigue Strength
310 MPa
Poisson's Ratio
0.3
Shear Modulus
84 GPa
Shear Strength
570 MPa
Tensile Strength: Ultimate (UTS)
810 MPa
Tensile Strength: Yield (Proof)
360 MPa

Hardness

Rockwell B Hardness
86

Physical

Density
9.0 g/cm 3

Thermal

Latent Heat of Fusion
320 J/g
Maximum Temperature: Mechanical
930 °C
Melting Completion (Liquidus)
1580 °C
Melting Onset (Solidus)
1520 °C
Specific Heat Capacity
410 J/kg-K
Thermal Expansion
11 µm/m-K
Thermal Shock Resistance
24 points

Calculated

Resilience: Ultimate (Unit Rupture Work)
300 MJ/m 3
Resilience: Unit (Modulus of Resilience)
300 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
22 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
22 points

Environmental

Base Metal Price
70 % relative
Embodied Carbon
13 kg CO 2 /kg material
Embodied Energy
170 MJ/kg
Embodied Energy
170 MJ/kg 75 x 10 3 BTU/lb
Embodied Water
270 L/kg
Embodied Water
270 L/kg 33 gal/lb
Registered Designations & Aliases
N10624UNS N10624 Nickel-Molybdenum Alloy
Standards

ASTM B333 ASTM B333: Standard Specification for Nickel-Molybdenum Alloy Plate, Sheet, and Strip

ASTM B333 ASTM B333: Standard Specification for Nickel-Molybdenum Alloy Plate, Sheet, and Strip ASTM B335: Standard Specification for Nickel-Molybdenum Alloy Rod ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube ASTM B564: Standard Specification for Nickel Alloy Forgings Microstructure of Superalloys, Madeleine Durand-Charre, 1998 Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971

ASTM B335 ASTM B335: Standard Specification for Nickel-Molybdenum Alloy Rod

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube