UNS N10003 Nickel Alloy
Nickel Alloys
Property Overview
Density8.9g/cm³
Elastic Modulus210GPa
Tensile Strength780MPa
Yield Strength320MPa
Brinell HardnessUnknown
Maximum Service Temperature930°C
Chemical Composition
C
0.040 to 0.080%
CR
6.0 to 8.0%
NI
64.8 to 79%
MO
15 to 18%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.015%
S
0 to 0.020%
CU
0 to 0.35%
V
0 to 0.5%
AL
0 to 0.5%
CO
0 to 0.2%
W
0 to 0.5%
B
0 to 0.010%
FE
0 to 5.0%
Mechanical
Elastic (Young's, Tensile) Modulus
210 GPa
Elongation at Break
42 %
Fatigue Strength
260 MPa
Poisson's Ratio
0.3
Shear Modulus
80 GPa
Shear Strength
540 MPa
Tensile Strength: Ultimate (UTS)
780 MPa
Tensile Strength: Yield (Proof)
320 MPa
Physical
Density
8.9 g/cm 3
Thermal
Latent Heat of Fusion
320 J/g
Maximum Temperature: Mechanical
930 °C
Melting Completion (Liquidus)
1520 °C
Melting Onset (Solidus)
1460 °C
Specific Heat Capacity
420 J/kg-K
Thermal Conductivity
12 W/m-K
Thermal Diffusivity
3.1 mm 2 /s
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
21 points
Electrical
Electrical Conductivity: Equal Volume
1.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.4 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
260 MJ/m 3
Resilience: Unit (Modulus of Resilience)
240 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
22 points
Strength to Weight: Axial
24 points
Strength to Weight: Bending
21 points
Environmental
Base Metal Price
70 % relative
Embodied Carbon
13 kg CO 2 /kg material
Embodied Energy
180 MJ/kg
Embodied Energy
180 MJ/kg 76 x 10 3 BTU/lb
Embodied Water
270 L/kg
Embodied Water
270 L/kg 32 gal/lb
Registered Designations & Aliases
N10003UNS N10003 Nickel Alloy
Standards
ASTM B434 ASTM B434: Standard Specification for Nickel-Molybdenum-Chromium-Iron Alloys (UNS N10003, UNS N10242) Plate, Sheet, and Strip
ASTM B434 ASTM B434: Standard Specification for Nickel-Molybdenum-Chromium-Iron Alloys (UNS N10003, UNS N10242) Plate, Sheet, and Strip ASTM B573: Standard Specification for Nickel-Molybdenum-Chromium-Iron Alloys (UNS N10003, N10242) Rod Microstructure of Superalloys, Madeleine Durand-Charre, 1998
ASTM B573 ASTM B573: Standard Specification for Nickel-Molybdenum-Chromium-Iron Alloys (UNS N10003, N10242) Rod