UNS N10001 (2.4810) Nickel-Molybdenum Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density9.2g/cm³

Elastic Modulus220GPa

Tensile Strength780MPa

Yield Strength350MPa

Brinell HardnessUnknown

Maximum Service Temperature900°C

Weight Calculator

Chemical Composition

0 to 0.050%

0 to 1.0%

58 to 69.8%

26 to 30%

0 to 1.0%

0 to 0.040%

0 to 0.030%

0.2 to 0.4%

0 to 2.5%

4.0 to 6.0%

Mechanical

Elastic (Young's, Tensile) Modulus

220 GPa

Elongation at Break

45 %

Fatigue Strength

300 MPa

Poisson's Ratio

0.31

Shear Modulus

84 GPa

Shear Strength

550 MPa

Tensile Strength: Ultimate (UTS)

780 MPa

Tensile Strength: Yield (Proof)

350 MPa

Hardness

Rockwell B Hardness

Physical

Density

9.2 g/cm 3

Thermal

Latent Heat of Fusion

320 J/g

Maximum Temperature: Mechanical

900 °C

Melting Completion (Liquidus)

1620 °C

Melting Onset (Solidus)

1570 °C

Specific Heat Capacity

390 J/kg-K

Thermal Expansion

10 µm/m-K

Thermal Shock Resistance

25 points

Calculated

Resilience: Ultimate (Unit Rupture Work)

290 MJ/m 3

Resilience: Unit (Modulus of Resilience)

280 kJ/m 3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

22 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

21 points

Environmental

Base Metal Price

75 % relative

Embodied Carbon

15 kg CO 2 /kg material

Embodied Energy

200 MJ/kg

Embodied Energy

200 MJ/kg 86 x 10 3 BTU/lb

Embodied Water

260 L/kg

Embodied Water

260 L/kg 32 gal/lb

Registered Designations & Aliases

2.4810N10001UNS N10001 (2.4810) Nickel-Molybdenum Alloy

Standards

ASTM B333 ASTM B333: Standard Specification for Nickel-Molybdenum Alloy Plate, Sheet, and Strip

ASTM B333 ASTM B333: Standard Specification for Nickel-Molybdenum Alloy Plate, Sheet, and Strip ASTM B335: Standard Specification for Nickel-Molybdenum Alloy Rod ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B335 ASTM B335: Standard Specification for Nickel-Molybdenum Alloy Rod

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube