UNS N08120 (2.4854) Nickel Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.2g/cm³

Elastic Modulus200GPa

Tensile Strength700MPa

Yield Strength310MPa

Brinell HardnessUnknown

Maximum Service Temperature1000°C

Weight Calculator

Chemical Composition

0.020 to 0.1%

23 to 27%

35 to 39%

0 to 2.5%

0 to 1.5%

0 to 1.0%

0.15 to 0.3%

0 to 0.040%

0 to 0.030%

0 to 0.5%

0.4 to 0.9%

0 to 0.2%

0 to 0.4%

0 to 3.0%

0 to 2.5%

0 to 0.010%

21 to 41.4%

Mechanical

Elastic (Young's, Tensile) Modulus

200 GPa

Elongation at Break

34 %

Fatigue Strength

230 MPa

Poisson's Ratio

0.28

Shear Modulus

79 GPa

Shear Strength

470 MPa

Tensile Strength: Ultimate (UTS)

700 MPa

Tensile Strength: Yield (Proof)

310 MPa

Physical

Density

8.2 g/cm 3

Thermal

Latent Heat of Fusion

310 J/g

Maximum Temperature: Mechanical

1000 °C

Melting Completion (Liquidus)

1420 °C

Melting Onset (Solidus)

1370 °C

Specific Heat Capacity

470 J/kg-K

Thermal Conductivity

11 W/m-K

Thermal Diffusivity

3.0 mm 2 /s

Thermal Expansion

14 µm/m-K

Thermal Shock Resistance

17 points

Calculated

PREN (Pitting Resistance)

Resilience: Ultimate (Unit Rupture Work)

190 MJ/m 3

Resilience: Unit (Modulus of Resilience)

240 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

21 points

Environmental

Base Metal Price

45 % relative

Embodied Carbon

7.2 kg CO 2 /kg material

Embodied Energy

100 MJ/kg

Embodied Energy

100 MJ/kg 44 x 10 3 BTU/lb

Embodied Water

240 L/kg

Embodied Water

240 L/kg 29 gal/lb

Registered Designations & Aliases

2.4854N08120UNS N08120 (2.4854) Nickel Alloy

Standards

ASTM B407 ASTM B407: Standard Specification for Nickel-Iron-Chromium Alloy Seamless Pipe and Tube

ASTM B408 ASTM B408: Standard Specification for Nickel-Iron-Chromium Alloy Rod and Bar

ASTM B408 ASTM B408: Standard Specification for Nickel-Iron-Chromium Alloy Rod and Bar ASTM B514: Standard Specification for Welded Nickel-Iron-Chromium Alloy Pipe ASTM B515: Standard Specification for Welded UNS N08120, UNS N08800, UNS N08810, and UNS N08811 Alloy Tubes ASTM B409: Standard Specification for Nickel-Iron-Chromium Alloy Plate, Sheet, and Strip ASTM B407: Standard Specification for Nickel-Iron-Chromium Alloy Seamless Pipe and Tube ASTM B564: Standard Specification for Nickel Alloy Forgings Microstructure of Superalloys, Madeleine Durand-Charre, 1998 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B409 ASTM B409: Standard Specification for Nickel-Iron-Chromium Alloy Plate, Sheet, and Strip

ASTM B514 ASTM B514: Standard Specification for Welded Nickel-Iron-Chromium Alloy Pipe

ASTM B515 ASTM B515: Standard Specification for Welded UNS N08120, UNS N08800, UNS N08810, and UNS N08811 Alloy Tubes

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings