UNS N06975 Nickel Alloy

Nickel Alloys

OverviewChemical CompositionMechanical PropertiesPhysical PropertiesOther Properties

Property Overview

Density8.3g/cm³
Elastic Modulus200GPa
Tensile Strength660MPa
Yield Strength250MPa
Brinell HardnessUnknown
Maximum Service Temperature1000°C
Weight Calculator

Chemical Composition

C
0 to 0.030%
CR
23 to 26%
NI
47 to 52%
MO
5.0 to 7.0%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.030%
S
0 to 0.030%
CU
0.7 to 1.2%
TI
0.7 to 1.5%
FE
10.2 to 23.6%

Mechanical

Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
45 %
Fatigue Strength
210 MPa
Poisson's Ratio
0.28
Shear Modulus
80 GPa
Shear Strength
470 MPa
Tensile Strength: Ultimate (UTS)
660 MPa
Tensile Strength: Yield (Proof)
250 MPa

Physical

Density
8.3 g/cm 3

Thermal

Latent Heat of Fusion
320 J/g
Maximum Temperature: Mechanical
1000 °C
Melting Completion (Liquidus)
1430 °C
Melting Onset (Solidus)
1380 °C
Specific Heat Capacity
460 J/kg-K
Thermal Expansion
13 µm/m-K
Thermal Shock Resistance
18 points

Calculated

Resilience: Ultimate (Unit Rupture Work)
240 MJ/m 3
Resilience: Unit (Modulus of Resilience)
150 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
20 points

Environmental

Base Metal Price
50 % relative
Embodied Carbon
8.9 kg CO 2 /kg material
Embodied Energy
120 MJ/kg
Embodied Energy
120 MJ/kg 53 x 10 3 BTU/lb
Embodied Water
270 L/kg
Embodied Water
270 L/kg 32 gal/lb
Registered Designations & Aliases
N06975UNS N06975 Nickel Alloy
Standards

ASTM B581 ASTM B581: Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Rod

ASTM B582 ASTM B582: Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Plate, Sheet, and Strip

ASTM B582 ASTM B582: Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Plate, Sheet, and Strip ASTM B581: Standard Specification for Nickel-Chromium-Iron-Molybdenum-Copper Alloy Rod ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube