UNS N06219 Nickel Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.5g/cm³

Elastic Modulus200GPa

Tensile Strength730MPa

Yield Strength300MPa

Brinell HardnessUnknown

Maximum Service Temperature980°C

Weight Calculator

Chemical Composition

0 to 0.050%

18 to 22%

60.8 to 72.3%

7.0 to 9.0%

0 to 0.5%

0.7 to 1.1%

0 to 0.020%

0 to 0.010%

0 to 0.5%

0 to 1.0%

2.0 to 4.0%

Mechanical

Elastic (Young's, Tensile) Modulus

200 GPa

Elongation at Break

48 %

Fatigue Strength

270 MPa

Poisson's Ratio

0.29

Shear Modulus

79 GPa

Shear Strength

520 MPa

Tensile Strength: Ultimate (UTS)

730 MPa

Tensile Strength: Yield (Proof)

300 MPa

Physical

Density

8.5 g/cm 3

Thermal

Latent Heat of Fusion

330 J/g

Maximum Temperature: Mechanical

980 °C

Melting Completion (Liquidus)

1430 °C

Melting Onset (Solidus)

1380 °C

Specific Heat Capacity

450 J/kg-K

Thermal Conductivity

10 W/m-K

Thermal Diffusivity

2.7 mm 2 /s

Thermal Expansion

12 µm/m-K

Thermal Shock Resistance

21 points

Electrical

Electrical Conductivity: Equal Volume

1.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

1.4 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)

280 MJ/m 3

Resilience: Unit (Modulus of Resilience)

230 kJ/m 3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

23 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

21 points

Environmental

Base Metal Price

60 % relative

Embodied Carbon

11 kg CO 2 /kg material

Embodied Energy

140 MJ/kg

Embodied Energy

140 MJ/kg 62 x 10 3 BTU/lb

Embodied Water

290 L/kg

Embodied Water

290 L/kg 34 gal/lb

Registered Designations & Aliases

N06219UNS N06219 Nickel Alloy

Standards

ASTM B443 ASTM B443: Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Plate, Sheet, and Strip

ASTM B443 ASTM B443: Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Plate, Sheet, and Strip ASTM B444: Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloys (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Pipe and Tube ASTM B704: Standard Specification for Welded UNS N06625, UNS N06219 and UNS N08825 Alloy Tubes ASTM B446: Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar ASTM B705: Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe ASTM B564: Standard Specification for Nickel Alloy Forgings Microstructure of Superalloys, Madeleine Durand-Charre, 1998 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B444 ASTM B444: Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloys (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Pipe and Tube

ASTM B446 ASTM B446: Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings

ASTM B704 ASTM B704: Standard Specification for Welded UNS N06625, UNS N06219 and UNS N08825 Alloy Tubes

ASTM B705 ASTM B705: Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe