UNS N06110 Nickel Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.6g/cm³

Elastic Modulus210GPa

Tensile Strength730MPa

Yield Strength330MPa

Brinell HardnessUnknown

Maximum Service Temperature1020°C

Weight Calculator

Chemical Composition

0 to 0.15%

28 to 33%

51 to 62%

9.0 to 12%

0 to 1.0%

0 to 0.5%

0 to 0.015%

0 to 0.5%

0 to 1.0%

1.0 to 4.0%

0 to 1.0%

Mechanical

Elastic (Young's, Tensile) Modulus

210 GPa

Elongation at Break

53 %

Fatigue Strength

320 MPa

Poisson's Ratio

0.28

Shear Modulus

84 GPa

Shear Strength

530 MPa

Tensile Strength: Ultimate (UTS)

730 MPa

Tensile Strength: Yield (Proof)

330 MPa

Physical

Density

8.6 g/cm 3

Thermal

Latent Heat of Fusion

340 J/g

Maximum Temperature: Mechanical

1020 °C

Melting Completion (Liquidus)

1490 °C

Melting Onset (Solidus)

1440 °C

Specific Heat Capacity

440 J/kg-K

Thermal Expansion

12 µm/m-K

Thermal Shock Resistance

20 points

Calculated

Resilience: Ultimate (Unit Rupture Work)

320 MJ/m 3

Resilience: Unit (Modulus of Resilience)

260 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

23 points

Strength to Weight: Axial

23 points

Strength to Weight: Bending

21 points

Environmental

Base Metal Price

65 % relative

Embodied Carbon

11 kg CO 2 /kg material

Embodied Energy

160 MJ/kg

Embodied Energy

160 MJ/kg 68 x 10 3 BTU/lb

Embodied Water

320 L/kg

Embodied Water

320 L/kg 38 gal/lb

Registered Designations & Aliases

N06110UNS N06110 Nickel Alloy

Standards

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings

ASTM B755 ASTM B755: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloys (UNS N06110) Plate, Sheet, and Strip

ASTM B755 ASTM B755: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloys (UNS N06110) Plate, Sheet, and Strip ASTM B756: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06110) Rod and Bar ASTM B757: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten-Alloys (UNS N06110) Welded Pipe ASTM B759: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloys (UNS N06110) Pipe and Tube ASTM B758: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloys (UNS N06110) Welded Tube ASTM B564: Standard Specification for Nickel Alloy Forgings Microstructure of Superalloys, Madeleine Durand-Charre, 1998 Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971

ASTM B756 ASTM B756: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06110) Rod and Bar

ASTM B757 ASTM B757: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten-Alloys (UNS N06110) Welded Pipe

ASTM B758 ASTM B758: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloys (UNS N06110) Welded Tube

ASTM B759 ASTM B759: Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloys (UNS N06110) Pipe and Tube