UNS N06058 Nickel Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.8g/cm³

Elastic Modulus220GPa

Tensile Strength860MPa

Yield Strength410MPa

Brinell HardnessUnknown

Maximum Service Temperature980°C

Weight Calculator

Chemical Composition

0 to 0.010%

20 to 23%

52.2 to 61%

19 to 21%

0 to 0.5%

0 to 0.1%

0.020 to 0.15%

0 to 0.015%

0 to 0.010%

0 to 0.5%

0 to 0.4%

0 to 0.3%

0 to 1.5%

Mechanical

Elastic (Young's, Tensile) Modulus

220 GPa

Elongation at Break

45 %

Fatigue Strength

350 MPa

Poisson's Ratio

0.29

Shear Modulus

86 GPa

Shear Strength

600 MPa

Tensile Strength: Ultimate (UTS)

860 MPa

Tensile Strength: Yield (Proof)

410 MPa

Physical

Density

8.8 g/cm 3

Thermal

Latent Heat of Fusion

330 J/g

Maximum Temperature: Mechanical

980 °C

Melting Completion (Liquidus)

1540 °C

Melting Onset (Solidus)

1490 °C

Specific Heat Capacity

420 J/kg-K

Thermal Conductivity

9.8 W/m-K

Thermal Diffusivity

2.6 mm 2 /s

Thermal Expansion

12 µm/m-K

Thermal Shock Resistance

23 points

Calculated

Resilience: Ultimate (Unit Rupture Work)

320 MJ/m 3

Resilience: Unit (Modulus of Resilience)

370 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

23 points

Strength to Weight: Axial

27 points

Strength to Weight: Bending

23 points

Environmental

Base Metal Price

70 % relative

Embodied Carbon

13 kg CO 2 /kg material

Embodied Energy

170 MJ/kg

Embodied Energy

170 MJ/kg 72 x 10 3 BTU/lb

Embodied Water

310 L/kg

Embodied Water

310 L/kg 37 gal/lb

Registered Designations & Aliases

N06058UNS N06058 Nickel Alloy

Standards

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings

ASTM B574 ASTM B574: Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod ASTM B575: Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, Low-Carbon Nickel- Chromium-Molybdenum-Tantalum, and Low-Carbon Nickel- Chromium-Molybdenum-Tungsten Alloy Plate, Sheet, and Strip ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube ASTM B564: Standard Specification for Nickel Alloy Forgings Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971 Nickel Alloys, Ulrich Heubner (editor), 1998

ASTM B575 ASTM B575: Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, Low-Carbon Nickel- Chromium-Molybdenum-Tantalum, and Low-Carbon Nickel- Chromium-Molybdenum-Tungsten Alloy Plate, Sheet, and Strip

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube