UNS N06045 Nickel-Chromium Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8g/cm³

Elastic Modulus200GPa

Tensile Strength690MPa

Yield Strength270MPa

Brinell HardnessUnknown

Maximum Service Temperature1010°C

Weight Calculator

Chemical Composition

0.050 to 0.12%

26 to 29%

45 to 50.4%

0 to 1.0%

2.5 to 3.0%

0 to 0.020%

0 to 0.010%

0 to 0.3%

0.030 to 0.090%

21 to 25%

Mechanical

Elastic (Young's, Tensile) Modulus

200 GPa

Elongation at Break

37 %

Fatigue Strength

210 MPa

Poisson's Ratio

0.28

Shear Modulus

77 GPa

Shear Strength

470 MPa

Tensile Strength: Ultimate (UTS)

690 MPa

Tensile Strength: Yield (Proof)

270 MPa

Physical

Density

8.0 g/cm 3

Thermal

Latent Heat of Fusion

350 J/g

Maximum Temperature: Mechanical

1010 °C

Melting Completion (Liquidus)

1350 °C

Melting Onset (Solidus)

1300 °C

Specific Heat Capacity

480 J/kg-K

Thermal Expansion

13 µm/m-K

Thermal Shock Resistance

18 points

Calculated

PREN (Pitting Resistance)

Resilience: Ultimate (Unit Rupture Work)

200 MJ/m 3

Resilience: Unit (Modulus of Resilience)

180 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

24 points

Strength to Weight: Bending

22 points

Environmental

Base Metal Price

42 % relative

Embodied Carbon

6.9 kg CO 2 /kg material

Embodied Energy

98 MJ/kg

Embodied Energy

98 MJ/kg 42 x 10 3 BTU/lb

Embodied Water

250 L/kg

Embodied Water

250 L/kg 30 gal/lb

Registered Designations & Aliases

N06045UNS N06045 Nickel-Chromium Alloy

Standards

ASTM B166 ASTM B166: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Rod, Bar, and Wire

ASTM B167 ASTM B167: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Seamless Pipe and Tube

ASTM B168 ASTM B168: Standard Specification Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Plate, Sheet, and Strip

ASTM B462 ASTM B462: Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service

ASTM B516 ASTM B516: Standard Specification for Welded Nickel-Chromium-Iron Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Tubes

ASTM B516 ASTM B516: Standard Specification for Welded Nickel-Chromium-Iron Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Tubes ASTM B517: Standard Specification for Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe ASTM B546: Standard Specification for Electric Fusion-Welded Ni-Cr-Co-Mo Alloy (UNS N06617), Ni-Fe-Cr-Si Alloys (UNS N08330 and UNS N08332), Ni-Cr-Fe-Al Alloy (UNS N06603), Ni-Cr-Fe Alloy (UNS N06025), and Ni-Cr-Fe-Si Alloy (UNS N06045) Pipe ASTM B166: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Rod, Bar, and Wire ASTM B167: Standard Specification for Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Seamless Pipe and Tube ASTM B168: Standard Specification Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Plate, Sheet, and Strip ASTM B462: Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service ASTM B564: Standard Specification for Nickel Alloy Forgings Microstructure of Superalloys, Madeleine Durand-Charre, 1998

ASTM B517 ASTM B517: Standard Specification for Welded Nickel-Chromium-Iron-Alloy (UNS N06600, UNS N06603, UNS N06025, and UNS N06045) Pipe

ASTM B546 ASTM B546: Standard Specification for Electric Fusion-Welded Ni-Cr-Co-Mo Alloy (UNS N06617), Ni-Fe-Cr-Si Alloys (UNS N08330 and UNS N08332), Ni-Cr-Fe-Al Alloy (UNS N06603), Ni-Cr-Fe Alloy (UNS N06025), and Ni-Cr-Fe-Si Alloy (UNS N06045) Pipe

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings