UNS N06035 (2.4643) Nickel-Chromium Alloy

Nickel Alloys

Overview Chemical Composition Mechanical Properties Physical Properties Other Properties

Property Overview

Density8.4g/cm³

Elastic Modulus210GPa

Tensile Strength660MPa

Yield Strength270MPa

Brinell HardnessUnknown

Maximum Service Temperature1030°C

Weight Calculator

Chemical Composition

0 to 0.050%

32.3 to 34.3%

51.1 to 60.2%

7.6 to 9.0%

0 to 0.5%

0 to 0.6%

0 to 0.030%

0 to 0.015%

0 to 0.3%

0 to 0.2%

0 to 0.4%

0 to 1.0%

0 to 0.6%

0 to 2.0%

Mechanical

Elastic (Young's, Tensile) Modulus

210 GPa

Elongation at Break

34 %

Fatigue Strength

200 MPa

Poisson's Ratio

0.28

Shear Modulus

84 GPa

Shear Strength

440 MPa

Tensile Strength: Ultimate (UTS)

660 MPa

Tensile Strength: Yield (Proof)

270 MPa

Physical

Density

8.4 g/cm 3

Thermal

Latent Heat of Fusion

340 J/g

Maximum Temperature: Mechanical

1030 °C

Melting Completion (Liquidus)

1440 °C

Melting Onset (Solidus)

1390 °C

Specific Heat Capacity

450 J/kg-K

Thermal Expansion

13 µm/m-K

Thermal Shock Resistance

17 points

Calculated

Resilience: Ultimate (Unit Rupture Work)

180 MJ/m 3

Resilience: Unit (Modulus of Resilience)

170 kJ/m 3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

22 points

Strength to Weight: Bending

20 points

Environmental

Base Metal Price

60 % relative

Embodied Carbon

10 kg CO 2 /kg material

Embodied Energy

140 MJ/kg

Embodied Energy

140 MJ/kg 61 x 10 3 BTU/lb

Embodied Water

330 L/kg

Embodied Water

330 L/kg 39 gal/lb

Registered Designations & Aliases

2.4643N06035UNS N06035 (2.4643) Nickel-Chromium Alloy

Standards

ASTM B462 ASTM B462: Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service

ASTM B564 ASTM B564: Standard Specification for Nickel Alloy Forgings

ASTM B574 ASTM B574: Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod

ASTM B575 ASTM B575: Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, Low-Carbon Nickel- Chromium-Molybdenum-Tantalum, and Low-Carbon Nickel- Chromium-Molybdenum-Tungsten Alloy Plate, Sheet, and Strip ASTM B574: Standard Specification for Low-Carbon Nickel-Chromium-Molybdenum, Low-Carbon Nickel-Molybdenum-Chromium-Tantalum, Low-Carbon Nickel-Chromium-Molybdenum-Copper, and Low-Carbon Nickel-Chromium-Molybdenum-Tungsten Alloy Rod ASTM B462: Standard Specification for Forged or Rolled UNS N06030, UNS N06022, UNS N06035, UNS N06200, UNS N06059, UNS N06686, UNS N08020, UNS N08024, UNS N08026, UNS N08367, UNS N10276, UNS N10665, UNS N10675, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R20033 Alloy Pipe Flanges, Forged Fittings, and Valves and Parts for Corrosive High-Temperature Service ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube ASTM B564: Standard Specification for Nickel Alloy Forgings Engineering Properties of Nickel and Nickel Alloys, John L. Everhart, 1971

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube