UNS N06002 Nickel Alloy

Nickel Alloys

OverviewChemical CompositionMechanical PropertiesPhysical PropertiesOther Properties

Property Overview

Density8.5g/cm³
Elastic Modulus210GPa
Tensile Strength760MPa
Yield Strength310MPa
Brinell HardnessUnknown
Maximum Service Temperature990°C
Weight Calculator

Chemical Composition

C
0.050 to 0.15%
CR
20.5 to 23%
NI
42.3 to 54%
MO
8.0 to 10%
MN
0 to 1.0%
SI
0 to 1.0%
P
0 to 0.040%
S
0 to 0.030%
CO
0.5 to 2.5%
W
0.2 to 1.0%
FE
17 to 20%

Mechanical

Elastic (Young's, Tensile) Modulus
210 GPa
Elongation at Break
41 %
Fatigue Strength
250 MPa
Poisson's Ratio
0.28
Shear Modulus
81 GPa
Shear Strength
520 MPa
Tensile Strength: Ultimate (UTS)
760 MPa
Tensile Strength: Yield (Proof)
310 MPa

Physical

Density
8.5 g/cm 3

Thermal

Latent Heat of Fusion
320 J/g
Maximum Temperature: Mechanical
990 °C
Melting Completion (Liquidus)
1360 °C
Melting Onset (Solidus)
1260 °C
Specific Heat Capacity
450 J/kg-K
Thermal Conductivity
9.9 W/m-K
Thermal Diffusivity
2.6 mm 2 /s
Thermal Expansion
14 µm/m-K
Thermal Shock Resistance
19 points

Electrical

Electrical Conductivity: Equal Volume
1.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.6 % IACS

Calculated

Resilience: Ultimate (Unit Rupture Work)
250 MJ/m 3
Resilience: Unit (Modulus of Resilience)
230 kJ/m 3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
22 points

Environmental

Base Metal Price
55 % relative
Embodied Carbon
9.3 kg CO 2 /kg material
Embodied Energy
130 MJ/kg
Embodied Energy
130 MJ/kg 54 x 10 3 BTU/lb
Embodied Water
270 L/kg
Embodied Water
270 L/kg 32 gal/lb
Registered Designations & Aliases
N06002UNS N06002 Nickel Alloy
Standards

ASTM B435 ASTM B435: Standard Specification for UNS N06002, UNS N06230, UNS N12160, and UNS R30556 Plate, Sheet, and Strip

ASTM B435 ASTM B435: Standard Specification for UNS N06002, UNS N06230, UNS N12160, and UNS R30556 Plate, Sheet, and Strip ASTM B572: Standard Specification for UNS N06002, UNS N06230, UNS N12160, and UNS R30556 Rod ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube Microstructure of Superalloys, Madeleine Durand-Charre, 1998 Welding Metallurgy and Weldability of Nickel-Base Alloys, John C. Lippold et al., 2009

ASTM B572 ASTM B572: Standard Specification for UNS N06002, UNS N06230, UNS N12160, and UNS R30556 Rod

ASTM B619 ASTM B619: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

ASTM B622 ASTM B622: Standard Specification for Seamless Nickel and Nickel-Cobalt Alloy Pipe and Tube

ASTM B626 ASTM B626: Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Tube