Nickel Beryllium Alloy 360 (N00360)
Nickel Alloys
annealed
Property Overview
Density8.3g/cm³
Elastic Modulus200GPa
Tensile Strength780MPa
Yield Strength380MPa
Brinell HardnessUnknown
Maximum Service TemperatureUnknown
Chemical Composition
Mechanical
Elastic (Young's, Tensile) Modulus
200 GPa
Elongation at Break
30 %
Fatigue Strength
260 MPa
Poisson's Ratio
0.3
Shear Modulus
77 GPa
Shear Strength
510 MPa
Tensile Strength: Ultimate (UTS)
780 MPa
Tensile Strength: Yield (Proof)
380 MPa
Physical
Density
8.3 g/cm 3
Thermal
Melting Completion (Liquidus)
1330 °C
Melting Onset (Solidus)
1200 °C
Specific Heat Capacity
460 J/kg-K
Thermal Conductivity
48 W/m-K
Thermal Diffusivity
13 mm 2 /s
Thermal Expansion
14 µm/m-K
Thermal Shock Resistance
19 points
Electrical
Electrical Conductivity: Equal Volume
5.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
5.4 % IACS
Calculated
Resilience: Ultimate (Unit Rupture Work)
190 MJ/m 3
Resilience: Unit (Modulus of Resilience)
360 kJ/m 3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
23 points
Registered Designations & Aliases
N00360Nickel Beryllium Alloy 360 (N00360)